Microwave Oven Electrophoresis Plating High Color Uniformity
Product Details
| Main Ingredients: | Organic Acid ;antirust Pigment | Application Field: | Microwave Oven |
|---|---|---|---|
| Performance: | Color Uniformity | Cooperation Case: | Galanz |
| Highlight |
Microwave Oven electrophoresis plating,uniform color electrophoresis plating,uniform color electrophoresis painting |
||
Product Description
Electrophoretic coating for domestic microwave oven
Product Introduction :
HS-6060ALB/HS-6600 White Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.
This product features shown below:
Excellent leveling coating,good bonding force and compatibility with plastic powder.
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
Good stability of bath can adaptable for a longer updating cycl
Main ingredients:
|
Pigment: titanium dioxide, kaolin,antirust pigment
|
Neutralizing agent: organic acid |
|
Additives: surface active agent, prevent shrinkage cavity agent,resistance to yellowing agent
|
|
Product quality data
| Project | Technical data | Test standard | ||
| Resin (HS-6060ALB) |
White Paste (HS-6600) | |||
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1400±400 | —— | HG/T 3334 |
| Appearance | —— | Milky white liquid | White viscous liquid,no agglomeration | Visual |
| Storage stability | No stratified state, and there were no obvious difference compared to before storage |
In 5-35 ℃ temperature 1 year | ||
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Filling tank proportion and method
⑴ Bath preparation
Ratio:
Resin 750.00-1000.00
Paste 250.00
DI water 1900.00-2200.00
Total 3 3025.00-3575.00
⑵ Ripening conditions
Sample quantity: 3000-4000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-34 ℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(165-175)℃×(20-30)min (Keeping temperature of parts coated)
Customers in the microwave oven industry:
Product Highlights
Electrophoretic coating for domestic microwave oven Product Introduction : HS-6060ALB/HS-6600 White Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic ...
High Throwing Power E Coating Car Body Paint Does Not Contain Heavy Metal
Solution for the Passenger car electrophoresis paint http://haolisen.com Product Introduction : HR-7001LB/HR-7010 Gray Cationic Epoxy Electrocoat for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS ...
ISO9001 High Weatherability Electrophoretic Paint For Commercial Vehicles
High weatherability electrophoretic paint for Commercial vehicles Product Introduction : HR-7001LB/HR-7010 Gray Cationic Epoxy Electrocoat for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS International ...
Gray Cationic Epoxy E Coat Paint , Electrolysis Anti Rust Paint For Cars
Solution for the bus electrophoresis paint Product Introduction HLS-5701LB/HLS-5750 Gray Cationic Epoxy Electrocoat for auto is the 7th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS International Chemical Industry Group. ...
Radiator White Epoxy Acrylic Cathodic Electrodeposition Paint Resistance To Yellowing
Solution for radiator electrodeposition coating Product Introduction : HS-5500LB/HS-5500 White epoxy acrylic cathodic electrophoretic coating for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. and get the national invention patent and ...