|Application Field:||Car Seats||Performance:||Good Corrosion Resistance|
|Cooperation Case:||FAWAY AUTOMOBILE，SAIC||Main Ingredients:||Carbon Black, Kaolin; Antirust Pigment|
Passenger cars and commercial vehicles seat Black electrophoresis paint
HL-1607LB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal,
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below:
The appearance of the coating is flat, delicate, smooth, uniform high gloss.
Good stability of bath can adaptable for a longer updating cycle.
The bath has strong anti-shrinkage and anti-pollution ability.
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
Coating fullness of good, better substrate hiding .
The main component Matrix resin:
polyurethane modified epoxy resin
Curing agent: totally enclosed multi-isocyanates
Neutralizing agent: organic acid
Solvent: alcohol ether
Additives: surface active agent, prevent shrinkage cavity agent
Pigment: Titanium pigment, carbon black, kaolin, antirust pigment
Product quality data:
|Project||Technical data||Test standard|
|Black Paste (HLS-1701A)|
|Appearance||——||Milky white liquid||Black viscous liquid,no agglomeration||Visual|
|Conductivity||25℃, μs/cm||1400±600||——||HG/T 3334|
No stratified state, and there were no obvious difference compared to before storage
|In 5-35 ℃ temperature 6 months|
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Filling tank proportion and method:
⑴ Bath preparation
DI water 2000.00
⑵ Ripening conditions
Sample quantity: 3000～3400g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-35℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(175-185)℃×(20-30)min (Keeping temperature of parts coated)
Bath on site management project:
Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:
|Classification||Project||Control Data||Testing frequency|
|Solid ( 120 ℃ /1h ,% )||14±4||--||once a day|
|PH||5.8-6.4||2.0-3.5||once a day|
|Conductivity ( μs/cm )||1200±400||2000±1000||once a day|
|P/B||0.08-0.15||once a week|
|L panel||Smooth horizontal plane and vertical plane without obvious differences||once a week|
|Solvent content (%)||0.5-1.8||once a week|
|Liquid level Fall head (cm )||10-15||once a day|
|ED voltage( V )||0-300||once a day|
|Break voltage ( V )||≥320||once a week|
|Bath temperature ( ℃ )||38-35||once a day|
|ED time( S )||60-180||once a day|
|UF － 1 Tank||Solid content (%)||≤2.0||once a day|
|UF － 2 Tank||Solid content (%)||≤0.8||once a day|
|Baking furnace||Provisions furnace temperature( ℃ )||180-190||once a day|
|Curing conditions||Drying temperature||
(175-185)℃×(20-30)min (With content holding time)
|once a day|
Product film performance:
|Appearance||Normal / abnormal||Normal||Ocular estimate|
|Cup drawing||mm ,≥||6||GB/T 9753|
|Water resistance||h,(23±2)℃,≥||240||GB/T 1733|
|Acid resistance||h,(50g/L H2SO4),≥||72||GB/T 9274|
|Alkali resistance||h,(50g/L NaOH),≥||72||GB/T 9274|
|*Salt spray resistance||h,(film thickness ≥ 20μm) ,≥||1000||GB/T 1771|
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment:
Circulation devices (including filter, fill the paint device)
DI water equipment
DC power supply and the power supply unit
Anode box (tube) and circulation device
Heat exchanging equipment
Storage, packaging and transportation:
This product is a water-borne industrial coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L Plastic barrel; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products, including paste resin, emulsions and additives should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5～35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.
This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.
If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now