Home ProductsED Paint

High Solid Content Electrophoretic Coating For Agricultural Machinery Industry

Certification
China HLS Coatings (Shanghai)Co.Ltd certification
China HLS Coatings (Shanghai)Co.Ltd certification
I'm Online Chat Now

High Solid Content Electrophoretic Coating For Agricultural Machinery Industry

High Solid Content Electrophoretic Coating For Agricultural Machinery Industry
High Solid Content Electrophoretic Coating For Agricultural Machinery Industry

Large Image :  High Solid Content Electrophoretic Coating For Agricultural Machinery Industry

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HLS-1701BLB/HLS-1701B
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day

High Solid Content Electrophoretic Coating For Agricultural Machinery Industry

Description
Application Field: Agricultural Machinery Cooperation Case: AGCO,BOYO
Performance: Better Substrate Hiding Main Ingredients: Titanium Pigment; Antirust Pigment
High Light:

electrophoretic painting process

,

electrolysis painting

Electrophoretic coating for agricultural machinery industry

 

Product Introduction

 

HLS-1701BLB/HLS-1701B Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.

 

This product features shown below:

 

 

The bath has strong anti-shrinkage and anti-pollution ability. 

Strong anti-corrosion properties, good salt spray resistance workpiece edge. 

etc.

 

The main component Matrix resin:

 

Neutralizing agent: organic acid

Solvent: alcohol ether

 

Filling tank proportion and method

 

⑴  Ripening conditions

Sample quantity: 3000~5000g
Container: 5L (Diameter 16cm)

Tank temperature:28-30 ℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)


 

 

Product film performance

 

Project Indicator Test standard
Appearance Normal / abnormal Normal Ocular estimate
Hardness 2H GB/T 6739
Cup drawing mm ,≥ 6 GB/T 9753
Adhesion Level 0 GB/T 9286
Flexibility mm 1 GB/T 1731
Impact kg·cm 50 GB/T 1732
Gloss 60 50-80 GB/T 9754
Water resistance h,(23±2)℃,≥ 240 GB/T 1733
Acid resistance h,(50g/L H2SO4),≥ 72 GB/T 9274
Alkali resistance h,(50g/L NaOH),≥ 48 GB/T 9274
*Salt spray resistanc​e h,(film thickness ≥ 20μm) ,≥ 1000 GB/T 1771

* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.

 

 

 

Storage, packaging and transportation

 

This product is a water-borne industrial coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L Plastic barrel; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products, including paste resin, emulsions and additives should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5~35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.



 

 