Product Details:
|
| Application Field: | Car Spring | Performance: | Good Flexibility |
|---|---|---|---|
| Cooperation Case: | Yuancheng Automobile | Main Ingredients: | Prevent Shrinkage Cavity Agent |
| High Light: | automobile cationic electrodeposition paint,vehicle cationic electrodeposition paint,vehicle electrodeposition coating |
||
Automotive spring electrophoresis paint
Product Introduction :
HLS-1701BLB/HLS-1701B Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal,
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below:
|
The bath has strong anti-shrink age andanti-pollutionability.
|
Coating fullness of good,better sub strate hiding. |
|
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
|
The appearance of the coating is flat, delicate, smooth, uniform high gloss. |
Main ingredients:
Curing agent:totally enclosed multi-isocyanates
Solvent:alcohol ether
Pigment: Titanium pigment, carbon black, kaolin, antirust pigment
Product film performance:
| Project | Indicator | Test standard | |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 72 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 48 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 1000 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.