Home ProductsCathodic Electrodeposition Paint

Oil Radiator Cathodic Electrodeposition Paint Coating Organic Acid

China HLS Coatings (Shanghai)Co.Ltd certification
China HLS Coatings (Shanghai)Co.Ltd certification
I'm Online Chat Now

Oil Radiator Cathodic Electrodeposition Paint Coating Organic Acid

Oil Radiator Cathodic Electrodeposition Paint Coating Organic Acid
Oil Radiator Cathodic Electrodeposition Paint Coating Organic Acid
Oil Radiator Cathodic Electrodeposition Paint Coating Organic Acid Oil Radiator Cathodic Electrodeposition Paint Coating Organic Acid

Large Image :  Oil Radiator Cathodic Electrodeposition Paint Coating Organic Acid

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HS-6500LB/HS-6500
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day

Oil Radiator Cathodic Electrodeposition Paint Coating Organic Acid

Main Ingredients: Organic Acid Application Field: Oil-radiator
Performance: Combustion Odour Cooperation Case: GREE,Midea,Singfun
High Light:

Cathodic Electrodeposition Paint Coating


Oil Radiator Electrodeposition Coating


Organic Acid Cathodic Electrodeposition Paint

Solution for oil-radiator electrodeposition coating


Product Introduction


HS-6500LB/HS-6500 White epoxy acrylic cathodic electrophoretic coating for auto is the 9th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd., and get the national invention patent and the Shanghai science and technology commission of high-tech transformation project.


It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin. The coating that does not contain tin element meet the latest environ-mental regulations of European Union, North America, Japan and other requirements in advance, which is the inevitable trend of future environ-mental coating and low cost; meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.


This product features shown below: 



High throwing power, good internal and external uniformity.



Simple control of bath and wide operation range is suitable for the operation specification and site equipment for different customers.



Low curing temperature, coating yellow degeneration resistance is good, suitable for electrodeposition primer, and then to spray or paint coating process, such as: oil heater, radiator, heater, lamps and lanterns, machinery, home appliances and hardware products and other industries.




Main ingredients:


Pigment: titanium dioxide, kaolin,antirust pigment


Neutralizing agent: organic acid


Additives: surface active agent, prevent shrinkage cavity agent,resistance to yellowing agent



Bath on site management project:


Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:


Classification Project Control Data Testing frequency
New bath Anolyte
Electrophoresis tank Ratio 1:3-4 --  
Ripening time 24-48 --  
Solid ( 120 ℃ /1h ,% ) 12±2 -- once a day
PH 5.3-5.8 2.0-3.5 once a day
Conductivity ( μs/cm ) 1000±400 1000±500 once a day
P/B 0.25-0.35 once a week
Solvent content (%) 0.8-1.5 once a week
Liquid level Fall head (cm ) 10-15 once a day
ED voltage( V ) 0-300 once a day
Break voltage ( V ) ≥350 once a week
Bath temperature ( ℃ ) 30±2 once a day
ED time( S ) 60~180 once a day
UF - 1 Tank Solid content (%) ≤2.0 once a day
UF - 2 Tank Solid content (%) ≤0.8 once a day
Baking furnace Provisions furnace temperature( ℃ ) 145-165 once a day
Curing conditions Drying temperature
(140-160)  ℃ ×(20-30)min (With content holding tim
once a day


Filling tank proportion and method


⑴ Bath preparation


Resin                     1020.00

Paste                       300.00

DI water                 3280.00

Total 3                    4600.00

⑵ Ripening conditions

Sample quantity:  4600g
Container: 5L (Diameter 16cm)

Tank temperature:28-30 ℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)

(3) Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 30±2℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions:(140-160)℃×(20-30)min (Keeping temperature of parts coated)