Special high anticorrosive performance electrophoretic paint for household appliances
Product Introduction :
|
HLS-1701ALB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
|
|
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal
|
|
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
|
Main ingredients:
|
Additives: surface active agent, prevent shrinkage cavity agent
|
|
|
Neutralizing agent: organic acid
|
Matrix resin: Acrylic modified epoxy resin |
Product quality data:
| Project | Technical data | Test standard | ||
| Resin (HLS-1701ALB) | Black Paste(HLS-1701A) | |||
| Appearance | —— | Milky white liquid | Black viscous liquid,no agglomeration | Visual |
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1400±600 | —— | HG/T 3334 |
| Storage stability | No stratified state, and there were no obvious difference compared to before storage |
In 5-35 ℃ temperature 1 year | ||
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Product film performance :
| Project | Indicator | Test standard | |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 50-90 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 72 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 48 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 1000 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Construction equipment:
Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment:
Electrophoresis tank
Circulation devices (including filter, fill the paint device)
DI water equipment
DC power supply and the power supply unit
Anode box (tube) and circulation device
Ultrafiltration device
Cleaning devices
Heat exchanging equipment
Curing device
Specification statement :
This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.
If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now
Fax: 86-021-69122952