Product Details:
|
| Application Field: | Auto Parts | Performance: | Film Smooth |
|---|---|---|---|
| Cooperation Case: | LEAR,WANXIANG | Main Ingredients: | Organic Acid ; Alcohol Ether |
| High Light: | electrophoretic coating,corrosion resistant coatings |
||
Automotive parts high anticorrosive performance electrophoretic paint
Product Introduction :
HL-1607LB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below:
|
The bath has strong anti-shrink age andanti-pollutionability.
|
Coating fullness of good,better sub strate hiding. |
|
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
|
The appearance of the coating is flat, delicate, smooth, uniform high gloss. |
Main ingredients :
| Pigment: carbon black, kaolin, antirust pigment | Solvent: alcohol ether |
| Additives: surface active agent, prevent shrinkage cavity agent | |
Product film performance :
| Project | Indicator | Test standard | |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 72 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 72 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 1000 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.