Product Details:
|
| Main Ingredients: | Alcohol Ether | Performance: | High Hardness |
|---|---|---|---|
| Application Field: | Groove Pipe Fitting | Cooperation Case: | MEIDE GROUP |
| Highlight: | edp paint,e coat aluminum |
||
Special color electrophoretic paint for groove pipe fitting
HS-6060BLB Color Epoxy acrylic Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, aluminum products, and stainless steel sheet etc. It is widely used in the electrophoresis coating of spring, hardware, home appliance, groove pipe fittings etc.
|
The appearance of the coating is flat, delicate, smooth, uniform high gloss
|
Good stability of bath can adaptable for a longer updating cycle |
|
The bath has strong anti-shrinkage and anti-pollution ability
|
Coating fullness of good, better substrate hiding |
1,Curing agent: totally enclosed multi-isocyanates
2,Solvent: alcohol ether
3,Pigment: Titanium pigment, Organic pigment, kaolin, antirust pigment
Product quality data :
| Project | Technical data | Test standard | ||
| Resin (HS-6060BLB) | Color Paste | |||
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1300±400 | —— | HG/T 3334 |
| Appearance | —— | Milky white liquid | viscous liquid,no agglomeration | Visual |
| Storage stability | No stratified state, and there were no obvious difference compared to before storage |
In 5-35 ℃ temperature 1 year | ||
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Product film performance :
| Project | Indicator | Test standard | |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 40-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 24 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 48 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 500 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Specification statement :
This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.
If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now
Customers in the elevator industry:
Fax: 86-021-69122952