Product Details:
|
| Application Field: | Lock | Cooperation Case: | SJ Group |
|---|---|---|---|
| Main Ingredients: | Titanium Pigment | Performance: | Good Corrosion Resistance |
| High Light: | edp paint,e coat aluminum |
||
Special color electrophoretic paint for lock
|
HS-6060BLB Color Epoxy acrylic Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
|
|
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal
|
|
such as: cold and hot rolled steel sheet, aluminum products, and stainless steel sheet etc. It is widely used in the electrophoresis coating of spring, hardware, home appliance, stationery, auto parts, electric car, groove pipe fittings etc.
|
①,High penetration and good uniformity of internal and external.
②,Have excellent corrosion resistance and weathering resistance, especially suitable for the bottom surface of a painting system.
③,Good stability of bath can adaptable for a longer updating cycle
Pigment:Titanium pigment, Organic pigment, kaolin, antirust pigment
Curing agent:totally enclosed multi-isocyanates
Solvent:alcohol ether
Matrix resin:acrylic modified epoxy resin
Bath on site management project :
Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:
| Classification | Project | Control Data | Testing frequency | |
| New bath | Anolyte | |||
| Electrophoresis tank | Ratio | 1:(6-8) | -- | |
| Ripening time | 24-48 | -- | ||
| Solid ( 120 ℃ /1h ,% ) | 15±5 | -- | once a day | |
| PH | 5.4-6.0 | 2.0-3.5 | once a day | |
| Conductivity ( μs/cm ) | 1000±500 | 1400±900 | once a day | |
| Solvent content (%) | 0.5-1.8 | once a week | ||
| Liquid level Fall head (cm ) | 10-15 | once a day | ||
| ED voltage( V ) | 0-300 | once a day | ||
| Break voltage ( V ) | ≥300 | once a week | ||
| Bath temperature ( ℃ ) | 30±2 | once a day | ||
| ED time( S ) | 60~180 | once a day | ||
| UF － 1 Tank | Solid content (%) | ≤2.0 | once a day | |
| UF － 2 Tank | Solid content (%) | ≤0.8 | once a day | |
| Baking furnace | Provisions furnace temperature( ℃ ) | 170-190 | once a day | |
| Curing conditions | Drying temperature | (165-185) ℃ ×(20-30)min (With content holding time) |
once a day | |
Specification statement :
This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.
If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now
Fax: 86-021-69122952