High Anticorrosive E Coating Car Body , Electrophoretic Lacquer Coating
Product Details
| Performance: | High Anticorrosive | Application Field: | High Anticorrosive Products |
|---|---|---|---|
| Cooperation Case: | MEIDE GROUP | Main Ingredients: | Polyurethane Modified Epoxy Resin |
| Highlight |
e coat aluminum,cataphoresis coating |
||
Product Description
High anticorrosive performance colorful electrophoretic coating
| The appearance of the coating is flat, delicate, smooth, uniform high gloss |
| Good stability of bath can adaptable for a longer updating cycle |
| The bath has strong anti-shrinkage and anti-pollution ability |
| Strong anti-corrosion properties |
| Coating fullness of good, better substrate hiding |
|
Matrix resin: acrylic modified epoxy resin
|
Curing agent: totally enclosed multi-isocyanates |
|
Neutralizing agent: organic acid
|
Solvent: alcohol ether |
|
Additives: surface active agent, prevent shrinkage cavity agent
|
Pigment: Titanium pigment, Organic pigment, kaolin, antirust pigment |
Product film performance :
| Project | Indicator | Test standard | |
| Appearance | Normal / Abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm,≥ | 6 | GB/T 9753 |
| Adhesion | level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | Kg.cm | 50 | GB/T 1732 |
| Gloss | 60° | 40-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃ ≥ | 240 | GB/T 1733 |
| Acid resistance | h(0.05N H2SO4) ≥ | 48 | GB/T 9274 |
| Alkali resistance | h(0.1N NaOH) ≥ | 48 | GB/T 9274 |
| *Salt spray resistance | film thickness ≥ 25μm | 500 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Specification statement :
This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.
If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now
Customers in the colorful industry :
Product Highlights
High anticorrosive performance colorful electrophoretic coating Product Introduction : HS-6060BLB Color Epoxy acrylic Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoret...
High Throwing Power E Coating Car Body Paint Does Not Contain Heavy Metal
Solution for the Passenger car electrophoresis paint http://haolisen.com Product Introduction : HR-7001LB/HR-7010 Gray Cationic Epoxy Electrocoat for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS ...
ISO9001 High Weatherability Electrophoretic Paint For Commercial Vehicles
High weatherability electrophoretic paint for Commercial vehicles Product Introduction : HR-7001LB/HR-7010 Gray Cationic Epoxy Electrocoat for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS International ...
Gray Cationic Epoxy E Coat Paint , Electrolysis Anti Rust Paint For Cars
Solution for the bus electrophoresis paint Product Introduction HLS-5701LB/HLS-5750 Gray Cationic Epoxy Electrocoat for auto is the 7th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS International Chemical Industry Group. ...
Radiator White Epoxy Acrylic Cathodic Electrodeposition Paint Resistance To Yellowing
Solution for radiator electrodeposition coating Product Introduction : HS-5500LB/HS-5500 White epoxy acrylic cathodic electrophoretic coating for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. and get the national invention patent and ...
Please use our online inquiry contact form below if you have any questions, our team will get back to you as soon as possible.