Home ProductsWhite Electrophoretic Coating

Low Temperature Curing White Electrophoretic Coating IATF16949 ISO9001 Approved

China HLS Coatings (Shanghai)Co.Ltd certification
China HLS Coatings (Shanghai)Co.Ltd certification
I'm Online Chat Now

Low Temperature Curing White Electrophoretic Coating IATF16949 ISO9001 Approved

Low Temperature Curing White Electrophoretic Coating IATF16949 ISO9001 Approved
Low Temperature Curing White Electrophoretic Coating IATF16949 ISO9001 Approved

Large Image :  Low Temperature Curing White Electrophoretic Coating IATF16949 ISO9001 Approved

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: CED-7101LB/HR-8010
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day

Low Temperature Curing White Electrophoretic Coating IATF16949 ISO9001 Approved

Application Field: Low Temperature Baking Products Main Ingredients: Totally Enclosed Multi-isocyanates
Performance: Low Cure Temperature Cooperation Case: JIUSHENG Bicycle
High Light:

ed coating


electrodeposition coating

Low temperature curing white electrophoresis paint


Product Introduction :


CED-7101LB/HR-8010 White epoxy acrylic cathodic electrophoretic coating for auto is the 9th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd., and get the national invention patent and the Shanghai science and technology commission of high-tech transformation project.It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin. The coating that does not contain tin element meet the latest environ-mental regulations of European Union, North America, Japan and other requirements in advance, which is the inevitable trend of future environ-mental coating and low cost; meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.

This product features shown below: 


Good stability of bath can adaptable for a longer updating cycle.


Simple control of bath and wide operation range is suitable for the operation specification and site equipment for different customers


Low curing temperature, coating yellow degeneration resistance is good, suitable for electrodeposition primer, and then to spray or paint coating process, such as: oil heater, radiator, heater, lamps and lanterns, machinery, home appliances and hardware products and other industries.

Main ingredients:


Matrix resin:Acrylic modified epoxy resin
Curing agent:Fully enclosed multi isocyanate
Neutralizing agent:organic acid
Additives:surface active agent, prevent shrinkage cavity agent,resistance to yellowing agent



Filling tank proportion and method:


⑴ Bath preparation


Resin                                      1868.00

Paste                                        467.00

DI water                                  2665.00

Total                                        5000.00

⑵ Ripening conditions

Sample quantity:  5000g
Container: 5L (Diameter 16cm)

Tank temperature:30 ±2 ℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)

(3) Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 30 ±2 ℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions:(140-160)℃×(20-30)min (Keeping temperature of parts coated)

Bath on site management project:


Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:


Classification Project Control Data Testing frequency
New bath Anolyte
Electrophoresis tank Ratio 1:3-5 --  
Ripening time 24-48 --  
Solid ( 120 ℃ /1h ,% ) 15±2 -- once a day
PH 4.0-5.0 2.0-3.5 once a day
Conductivity ( μs/cm ) 600±300 1000±500 once a day
P/B 0.35-0.45 once a week
Solvent content (%) 1.2-2.0 once a week
Liquid level Fall head (cm ) 10-15 once a day
ED voltage( V ) 0-300 once a day
Break voltage ( V ) ≥350 once a week
Bath temperature ( ℃ ) 30±2 once a day
ED time( S ) 60~180 once a day
UF - 1 Tank Solid content (%) ≤2.0 once a day
UF - 2 Tank Solid content (%) ≤0.8 once a day
Baking furnace Provisions furnace temperature( ℃ ) 160-180 once a day
Curing conditions Drying temperature
(140-160) ℃ ×(20-30)min (With content holding time)
once a day


Construction equipment


Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment: 

Electrophoresis tank 

Circulation devices (including filter, fill the paint device) 

DI water equipment 

DC power supply and the power supply unit 

Anode box (tube) and circulation device 

Ultrafiltration device 

Cleaning devices 

Heat exchanging equipment 

Curing device


Specification statement


This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.

If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now



Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)