Non - Inflammable Cationic Epoxy Electrocoat For Engineering Mechanical

China HLS Coatings (Shanghai)Co.Ltd certification
China HLS Coatings (Shanghai)Co.Ltd certification
I'm Online Chat Now

Non - Inflammable Cationic Epoxy Electrocoat For Engineering Mechanical

Non - Inflammable Cationic Epoxy Electrocoat For Engineering Mechanical
Non - Inflammable Cationic Epoxy Electrocoat For Engineering Mechanical

Large Image :  Non - Inflammable Cationic Epoxy Electrocoat For Engineering Mechanical

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HS-6060LB/HS-2516G
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day

Non - Inflammable Cationic Epoxy Electrocoat For Engineering Mechanical

Shelf Life: 1 Year Product Name: Electrophoretic Paint
Application Field: Engineering Mechanical Performance: Film Is Uniform
Cooperation Case: SANY,LION CHINA Main Ingredients: Organic Acid ;antirust Pigment
High Light:

electrophoretic painting


epd coating

Engineering mechanical grey electrophoretic paint


Product Introduction:


HS-6060LB/HS-2516G Gray Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.


This product features shown below:


The bath has strong anti-shrinkage and anti-pollution ability.  Good stability of bath can adaptable for a longer updating cycle. 
Coating fullness of good, better substrate hiding . Excellent leveling coating,good bonding force and compatibility with plastic powder.



The main component Matrix resin:


Matrix resin​:polyurethane modified epoxy resin


Curing agent:totally enclosed multi-isocyanates


Additives: surface active agent, prevent shrinkage cavity agent


Product quality data :


Project Technical data Test standard
Gray Paste (HS-2516G)
Appearance —— Milky white liquid Gray viscous liquid,no agglomeration Visual
pH 25℃ 6.0±1.0 —— GB/T 9724
Conductivity 25℃, μs/cm 1400±400 —— HG/T 3334
Storage stability
No stratified state, and there were no obvious difference compared to before storage
In 5-35 ℃ temperature 1 year 

Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution


Filling tank proportion and method:


Bath preparation


Resin                                 1000.00-1250.00

Paste                                                 250.00

DI water                             1900.00-2200.00

Total                                  3025.00-3575.00



Bath on site management project:


Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:


Classification Project Control Data Testing frequency
New bath Anolyte
Electrophoresis tank Ratio 1:(3.5-4.5) -- --
Ripening time 24-48 -- --
Solid ( 120 ℃ /1h ,% ) 14±4 -- once a day
PH 5.7-6.2 2.0-3.5 once a day
Conductivity ( μs/cm ) 1200±400 1500±500 once a day
P/B 0.20-0.30 once a week
L panel Smooth horizontal plane and vertical plane without obvious differences once a week
Solvent content (%) 0.5-1.8 once a week
Liquid level Fall head (cm ) 10-15 once a day
ED voltage( V ) 0-300 once a day
Break voltage ( V ) ≥320 once a week
Bath temperature ( ℃ ) 30-36 once a day
ED time( S ) 60-180 once a day
UF - 1 Tank Solid content (%) ≤2.0 once a day
UF - 2 Tank Solid content (%) ≤0.8 once a day
Baking furnace Provisions furnace temperature( ℃ ) 170-185 once a day
Curing conditions Drying temperature
(165-180)℃×(20-30)min (With content holding time)
once a day


Storage, packaging and transportation:


This product is a water-borne industrial coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L Plastic barrel; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products, including paste resin, emulsions and additives should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5~35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.


Customer production site​:


Non - Inflammable Cationic Epoxy Electrocoat For Engineering Mechanical 0

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)