Product Details:
|
| Application Field: | Colorful Products | Performance: | Color Bright Beautiful |
|---|---|---|---|
| Cooperation Case: | MEIDE GROUP，Mingli Spring | Main Ingredients: | Organic Acid |
| High Light: | e coat painting,electrophoretic painting process |
||
Application of colorful electrophoresis coating industry
Product Introduction :
HS-6060BLB Color Epoxy acrylic Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, aluminum products, and stainless steel sheet etc. It is widely used in the electrophoresis coating of spring, hardware, home appliance, stationery, auto parts, electric car, groove pipe fittings etc
This product features shown below:
| The appearance of the coating is flat, delicate, smooth. |
| Good stability of bath can adaptable for a longer updating cycle. |
| Strong anti-corrosion properties, good salt spray resistance workpiece edge. |
| Coating fullness of good, better substrate hiding . |
The main component :
Pigment: Titanium pigment, carbon black, kaolin, antirust pigment
Neutralizing agent: organic acid
Curing agent: totally enclosed multi-isocyanates
Matrix resin: polyurethane modified epoxy resin
Product film performance :
| Project | Indicator | Test standard | |
| Appearance | Normal / Abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm,≥ | 6 | GB/T 9753 |
| Adhesion | level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | Kg.cm | 50 | GB/T 1732 |
| Gloss | 60° | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃ ≥ | 240 | GB/T 1733 |
| Acid resistance | h(0.05N H2SO4) ≥ | 48 | GB/T 9274 |
| Alkali resistance | h(0.1N NaOH) ≥ | 48 | GB/T 9274 |
| *Salt spray resistance | film thickness ≥ 20μm | 500 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.