Two Component ED Black Coating Low Temperature Curing For Car Shock Absorber

Two Component ED Black Coating Low Temperature Curing For Car Shock Absorber
Two Component ED Black Coating Low Temperature Curing For Car Shock Absorber Two Component ED Black Coating Low Temperature Curing For Car Shock Absorber

Large Image :  Two Component ED Black Coating Low Temperature Curing For Car Shock Absorber

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: OHT-825/OHT-825
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day

Two Component ED Black Coating Low Temperature Curing For Car Shock Absorber

Description
Application Field: Car Shock Absorber Main Ingredients: Organic Acid ;antirust Pigment
Cooperation Case: ZHONGDING Performance: Low Temperature
High Light:

black e coat

,

black edp coating

Car shock absorber black electrophoresis paint by Low temperature curing ​

 

Product Introduction :

 

OHT-825/OHT-825 Ultra Low temperature Black Cationic Epoxy Electrocoat, is HLS Paint (Shanghai) Co., Ltd. the ninth generation of independent research and development of electrophoretic coating. The lead, cadmium, chromium, mercury and other heavy metals, two-component aqueous dispersion resin. At the same time, inherited the characteristics of several generations of product quality, OHT-825 on galvanized steel sheet has good adaptability, almost at the bottom of all the metal material coating, such as: cold rolled steel, galvanized steel, aluminum, stainless steel plate, rubber parts, zinc and aluminum alloy plate, such as applicable.

 

This product features shown below: 

High penetration and good uniformity of internal and external. 

Excellent leveling and coating, coating, coating binding force and supporting good 

Particularly suitable for high temperature baking of the workpiece, in particular, rubber and metal binding parts and zinc aluminum alloy material. 

 

Main ingredients:

 

 

Neutralizing agent: organic acid

Solvent: alcohol ether

 

Product quality data

 

Project Technical data Test standard
Resin
(OHT-825)
Black Paste (OHT-825)
Appearance —— Milky white liquid Black viscous liquid,no agglomeration Visual
pH 25℃ 6.0±1.0 —— GB/T 9724
Conductivity 25℃, μs/cm 1400±500 —— HG/T 3334
Storage stability
No stratified state, and there were no obvious difference compared to before storage
In 5-35 ℃ temperature 1 year

Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution

 

Coating conditions

 

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 28-35℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions: (130-140)℃×(20-30)min (Keeping temperature of parts coated)


 

Bath on site management project

 

Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:

 

Classification Project Control Data Testing frequency
New bath Anolyte
Electrophoresis tank Ratio 1:(4-5) --  
Ripening time 24-48 --  
Solid ( 120 ℃ /1h ,% ) 10-20 -- once a day
PH 5.1-5.8 2.0-3.5 once a day
Conductivity ( μs/cm ) 1200±400 1500±700 once a day
P/B 0.1-0.20 once a week
L panel Smooth horizontal plane and vertical plane without obvious differences once a week
Solvent content (%) 2.0-4.5 once a week
Liquid level Fall head (cm ) 10-15 once a day
ED voltage( V ) 0-280 once a day
Break voltage ( V ) 350 once a week
Bath temperature ( ℃ ) 28-35 once a day
ED time( S ) 60~180 once a day
UF - 1 Tank Solid content (%) ≤2.0 once a day
UF - 2 Tank Solid content (%) ≤0.8 once a day
Baking furnace Provisions furnace temperature( ℃ ) 135-145 once a day
Curing conditions Drying temperature
(130-140) ×(20-30)min (With content holding time)
once a day

 

 

Storage, packaging and transportation

 

This product is a water-borne industrial coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L Plastic barrel; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products, including paste resin, emulsions and additives should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5~35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.
 

Two Component ED Black Coating Low Temperature Curing For Car Shock Absorber 0

 

 

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)