Low Temperature Curing Black Electrophoresis Paint For Shock Absorber And Compressor

China HLS Coatings (Shanghai)Co.Ltd certification
China HLS Coatings (Shanghai)Co.Ltd certification
I'm Online Chat Now

Low Temperature Curing Black Electrophoresis Paint For Shock Absorber And Compressor

Low Temperature Curing Black Electrophoresis Paint For Shock Absorber And Compressor
Low Temperature Curing Black Electrophoresis Paint For Shock Absorber And Compressor

Large Image :  Low Temperature Curing Black Electrophoresis Paint For Shock Absorber And Compressor

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: OHT-825/OHT-825
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day
Detailed Product Description
Application Field: Low Temperature Baking Product Performance: Low Cure Temperature
Cooperation Case: Jiaxipera,embraco Main Ingredients: Organic Acid
Cure Temperature: 130-140℃ Color: Black.
High Light:

black e coat

,

black edp coating

Low temperature curing Black electrophoresis paint for shock absorber and Compressor

 

Product Introduction :

 

OHT-825/OHT-825 Ultra Low temperature Black Cationic Epoxy Electrocoat, is HLS Paint (Shanghai) Co., Ltd. the ninth generation of independent research and development of electrophoretic coating. The lead, cadmium, chromium, mercury and other heavy metals, two-component aqueous dispersion resin. At the same time, inherited the characteristics of several generations of product quality, OHT-825 on galvanized steel sheet has good adaptability, almost at the bottom of all the metal material coating, such as: cold rolled steel, galvanized steel, aluminum, stainless steel plate, rubber parts, zinc and aluminum alloy plate, such as applicable.

 

This product features shown below: 

 

The appearance of the coating is flat, delicate, smooth. 
Good stability of bath can adaptable for a longer updating cycle. 
The bath has strong anti-shrinkage and anti-pollution ability. 
The ability of corrosion resistance is strong, and the edge of the workpiece is good in salt spray resistance 

 

Main ingredients:

 

Curing agent: Modified low temperature curing agent
Matrix resin: Acrylic modified epoxy resin
Solvent: alcohol ether
Pigment: carbon black, kaolin, antirust pigment

 

 
Filling tank proportion and method
 
⑴ Bath preparation
Ratio:
Resin                        1000.00 -1250.00
Paste                                         250.00
DI water                                   1000.00


Total                         2250.00 -2500.00
⑵ Ripening conditions
Sample quantity: 2250~2500g
Container: 4L (Diameter 16cm)
Tank temperature: 28~32℃
Time: 24~48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)


(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-35℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions: (130-140)℃×(20-30)min (Keeping temperature of parts coated)
 


Construction equipment

 

Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment: 

Electrophoresis tank 

Circulation devices (including filter, fill the paint device) 

DI water equipment 

DC power supply and the power supply unit 

Anode box (tube) and circulation device 

Ultrafiltration device 

Cleaning devices 

Heat exchanging equipment 

Curing device

 

 

Annex 1

 

Low Temperature Curing Black Electrophoresis Paint For Shock Absorber And Compressor 0