Send Message
Home ProductsE Coat Car Coating

Corrosion Resistance Ecoat Car Coating , Electrophoretic Lacquer Coating

Certification
China HLS Coatings (Shanghai)Co.Ltd certification
China HLS Coatings (Shanghai)Co.Ltd certification
I'm Online Chat Now

Corrosion Resistance Ecoat Car Coating , Electrophoretic Lacquer Coating

Corrosion Resistance Ecoat Car Coating , Electrophoretic Lacquer Coating
Corrosion Resistance Ecoat Car Coating , Electrophoretic Lacquer Coating

Large Image :  Corrosion Resistance Ecoat Car Coating , Electrophoretic Lacquer Coating

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HL-1607LB/HLS-1701A
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day

Corrosion Resistance Ecoat Car Coating , Electrophoretic Lacquer Coating

Description
Application Field: Motorcycle Frame Main Ingredients: Organic Acid
Cooperation Case: DAYUN Performance: Good Corrosion Resistance
Highlight:

e coating solutions

,

car body protection coating

Solution for the Motorcycle frame electrophoresis paint

 

 

Product Introduction

 

HL-1607LB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.

It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.

 

This product features shown below:

The appearance of the coating is flat, delicate, smooth, uniform high gloss.

 

Stronganti-corrosionproperties,goodsaltsprayresistanceworkpieceedge.

 

Excellent leveling coating,good bonding for ceand compatibility with plastic powder

 

.

The main component Matrix resin:

 

1,Neutralizing agent: organic acid

 

2,Solvent: alcohol ether

 

3,Pigment: carbon black, kaolin, antirust pigment

 

 

Product quality data:

 

Project Technical data Test standard
Resin
(HL-1607LB)
Black Paste (HLS-1701A)
Appearance —— Milky white liquid Black viscous liquid,no agglomeration Visual
pH 25℃ 6.0±1.0 —— GB/T 9724
Conductivity 25℃, μs/cm 1400±600 —— HG/T 3334
Storage stability
No stratified state, and there were no obvious difference compared to before storage
In 5-35 ℃ temperature 1 year 

Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution

 


Filling tank proportion and method

 

⑴ Bath preparation

Ratio:

Resin                      800.00-1200.00

Paste                                    200.00

DI water                              2000.00


Total                                   3400.00

⑵ Ripening conditions

Sample quantity: 3000~3400g
Container: 5L (Diameter 16cm)

Tank temperature:28-30 ℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)


(3) Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 30-35℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions:(175-185)℃×(20-30)min (Keeping temperature of parts coated)

 

Customer production site​:

 

Corrosion Resistance Ecoat Car Coating , Electrophoretic Lacquer Coating 0

 

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Fax: 86-021-69122952

Send your inquiry directly to us (0 / 3000)