Auto Parts Cathodic Electrophoretic Coating Black Color With High Substrate Hiding

Auto Parts Cathodic Electrophoretic Coating Black Color With High Substrate Hiding
Auto Parts Cathodic Electrophoretic Coating Black Color With High Substrate Hiding

Large Image :  Auto Parts Cathodic Electrophoretic Coating Black Color With High Substrate Hiding

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HL-1607LB/HLS-1701A
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day
Detailed Product Description
Application Field: Auto Parts Performance: Film Smooth
Cooperation Case: FUWA,FORTAI,FANGDA Main Ingredients: Totally Enclosed Multi-isocyanates
High Light:

electrophoresis coating

,

cathodic epoxy electrocoat

Auto parts electrodeposition coating solution

 

Product Introduction

 

 

HL-1607LB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.

 

 

 

This product features shown below: 

 

The bath has strong anti-shrink age andanti-pollutionability.
Coating fullness of good,better sub strate hiding. 
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
The appearance of the coating is flat, delicate, smooth, uniform high gloss.

 

Main ingredients

 

Matrix resin: Acrylic modified epoxy resin

 

Pigment: carbon black, kaolin, antirust pigment

 

Additives:surface active agent, prevent shrinkage cavity agent

 

Product quality data

 

Project Technical data Test standard
Resin
(HL-1607LB)

Black Paste 

(HLS-1701A)

Appearance —— Milky white liquid Black viscous liquid,no agglomeration Visual
pH 25℃ 6.0±1.0 —— GB/T 9724
Conductivity 25℃, μs/cm 1400±600 —— HG/T 3334
Storage stability
No stratified state, and there were no obvious difference compared to before storage
In 5-35 ℃ temperature 1 year

Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution

 

 

Product film performance

 

Project Indicator Test standard
Appearance Normal / abnormal Normal Ocular estimate
Hardness 2H GB/T 6739
Cup drawing mm ,≥ 6 GB/T 9753
Adhesion Level 0 GB/T 9286
Flexibility mm 1 GB/T 1731
Impact kg·cm 50 GB/T 1732
Gloss 60 50-80 GB/T 9754
Water resistance h,(23±2)℃,≥ 240 GB/T 1733
Acid resistance h,(50g/L H2SO4),≥ 72 GB/T 9274
Alkali resistance h,(50g/L NaOH),≥ 72 GB/T 9274
*Salt spray resistanc​e h,(film thickness ≥ 20μm) ,≥ 1000 GB/T 1771

* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.


 

Customer production site:

 

Auto Parts Cathodic Electrophoretic Coating Black Color With High Substrate Hiding 0

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)