Metallic effect comparable to paint;
comparable to the color stability of plain powder;
Better acid and alkali resistance
HLS ACE-Standard series applied to 0.8mm chrome aluminum plate test plates (coating thickness 60-90 um)
| project | standard | HLS ACE-Standard Series |
| gloss | EN ISO 2813 (60°) | ≧90 |
| finish | visual | smooth |
| adhesion | EN ISO 2409 (2 mm) | Cross-cut rating Gt0 |
| impact resistance | ASTM D 2794 (15.9mm) punch diameter | More than 80 inches-pounds,pull adhesive tape , no film peeling |
| cupping tese | EN ISO 1520 | Indentation depth in excess 10mm ,no film cracking |
| bending performance | EN ISO 1519 | cylindrical axis bend test,passing 3mm axis diameter |
| film hardness | EN ISO 2815 | >85 Buckholz Hardness:>85 |
| Salt spray test | ASTM B 117 | After 500H ,no blistering ,no film peeling |
| humidity resistance | EN ISO 6270-2 | After 500H ,no foaming,no film peeling ,side corrosion max. 1mm |
|
UV resistance |
DIN EN ISO 11507 (UVB - 313) | Cycle: 50℃ UV 4 hours,40℃condensate 4 hours, no-powdering after 168H, excellent gloss retention and color stability |
|
Accelerated weathering |
DIN EN ISO 11507 (UVA – 340) | Cycle: 60℃UV 8 hours,45℃ condensate 4 hours, non-powdering after 500 hours, excellent gloss retention and color stability |