Product Details:
|
Main Ingredients: | Prevent Shrinkage Cavity Agent | Application Field: | Grader |
---|---|---|---|
Performance: | Film Is Bright | Cooperation Case: | SANY |
High Light: | cationic epoxy electrocoat,edp coating |
Solution for electrophoresis paint for grader
HS-6060LB/HS-2568G Gray Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal,
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.
1,Strong anti-corrosion properties, good salt spray resistance workpiece edge.
2,Good stability of bath can adaptable for a longer updating cycle.
3,Excellent leveling coating,good bonding force and compatibility with plastic powder
Matrix resin: polyurethane modified epoxy resin
|
Curing agent: totally enclosed multi-isocyanates |
Neutralizing agent: organic acid
|
Additives: surface active agent, prevent shrinkage cavity agent |
Bath on site management project :
Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:
Classification | Project | Control Data | Testing frequency | |
New bath | Anolyte | |||
Electrophoresis tank | Ratio | 1:(4-5) | -- | |
Ripening time | 24-48 | -- | ||
Solid ( 120 ℃ /1h ,% ) | 14±4 | -- | once a day | |
PH | 5.7-6.2 | 2.0-3.5 | once a day | |
Conductivity ( μs/cm ) | 1200±400 | 1500±500 | once a day | |
P/B | 0.20-0.30 | once a week | ||
Solvent content (%) | 0.8-1.5 | once a week | ||
Liquid level Fall head (cm ) | 10-15 | once a day | ||
ED voltage( V ) | 0-300 | once a day | ||
Break voltage ( V ) | ≥320 | once a week | ||
Bath temperature ( ℃ ) | 28-35 | once a day | ||
ED time( S ) | 60~180 | once a day | ||
UF - 1 Tank | Solid content (%) | ≤2.0 | once a day | |
UF - 2 Tank | Solid content (%) | ≤0.8 | once a day | |
Baking furnace | Provisions furnace temperature( ℃ ) | 180-190 | once a day | |
Curing conditions | Drying temperature | (175-185) ℃ ×(15-20)min (With content holding time) |
once a day |
Construction equipment:
Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment:
Electrophoresis tank
|
Circulation devices (including filter, fill the paint device) | DI water equipment |
DC power supply and the power supply unit
|
Anode box (tube) and circulation device | Ultrafiltration device |
Cleaning devices
|
Heat exchanging equipment | Curing device |
If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now
Fax: 86-021-69122952