Easy Coat Low Temperature Curing Electrophoresis Paint For Compressor

video play

Large Image :  Easy Coat Low Temperature Curing Electrophoresis Paint For Compressor

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: OHT-825/OHT-825
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day
Detailed Product Description
Application Field: Compressor Main Ingredients: Alcohol Ether
Performance: Good Salt Mist Cooperation Case: HUAYI,QIANGJIANG
High Light:

edp painting


anti rust coating for cars

Low temperature curing electrophoresis paint for Compressor


Product Introduction :



OHT-825/OHT-825 Ultra Low temperature Black Cationic Epoxy Electrocoat, is HLS Paint (Shanghai) Co., Ltd. the ninth generation of independent research and development of electrophoretic coating. The lead, cadmium, chromium, mercury and other heavy metals, two-component aqueous dispersion resin. At the same time, inherited the characteristics of several generations of product quality, OHT-825 on galvanized steel sheet has good adaptability, almost at the bottom of all the metal material coating,


such as: cold rolled steel, galvanized steel, aluminum, stainless steel plate, rubber parts, zinc and aluminum alloy plate, such as applicable



This product features shown below : 



Good stability of bath can adaptable for a longer updating cycle


High penetration and good uniformity of internal and external.


Particularly suitable for high temperature baking of the workpiece, in particular, rubber and metal binding parts and zinc aluminum alloy material



Main ingredients:



Additives: surface active agent, prevent shrinkage cavity agent



Pigment: carbon black, kaolin, antirust pigment



Neutralizing agent: organic acid



Matrix resin: Acrylic modified epoxy resin




Filling tank proportion and method :


⑴ Bath preparation


Resin                                                   1000.00 -1250.00

Paste                                                                    250.00

DI water                                                              1000.00

Total                                                     2250.00 -2500.00

(2)Ripening conditions

Sample quantity: 2250~2500g
Container: 4L (Diameter 16cm)

Tank temperature: 28~32℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)

(3) Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 28-35℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions: (130-140)℃×(20-30)min (Keeping temperature of parts coated)


Specification statement


This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.

If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now


Customer production site :


Easy Coat Low Temperature Curing Electrophoresis Paint For Compressor 0


Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)