Product Details:
|
Application Field: | Pipeline | Cooperation Case: | MEIDE GROUP |
---|---|---|---|
Main Ingredients: | Alcohol Ether | Performance: | Film Smooth |
High Light: | electrodeposition painting process,electrodeposition coating process automobile bodies |
Solution for pipeline electrophoresis paint
The appearance of the coating is flat, delicate, smooth, uniform high gloss |
Good stability of bath can adaptable for a longer updating cycle |
The bath has strong anti-shrinkage and anti-pollution ability |
Strong anti-corrosion properties |
Coating fullness of good, better substrate hiding |
Matrix resin: acrylic modified epoxy resin
|
Curing agent: totally enclosed multi-isocyanates |
Neutralizing agent: organic acid
|
Solvent: alcohol ether |
Additives: surface active agent, prevent shrinkage cavity agent
|
Pigment: Titanium pigment, Organic pigment, kaolin, antirust pigment |
Filling tank proportion and method :
⑴ Bath preparation
Ratio:
Resin 750.00-1000.00
Paste 250.00
DI water 1900.00-2200.00
Total 3025.00-3575.00
⑵ Ripening conditions
Sample quantity: 3000~4000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24~48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-34℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(180-185)℃×(20-30)min (Keeping temperature of parts coated)
Customers in the pipeline industry :
Fax: 86-021-69122952