Product Details:
|
| Performance: | Film Is Uniform | Cooperation Case: | SANY,LION CHINA |
|---|---|---|---|
| Main Ingredients: | Titanium Pigment | Application Field: | Engineering Mechanical |
| High Light: | electrophoretic coating,ced painting |
||
High anticorrosive performance electrophoretic paint for engineering machinery
Product Introduction :
HLS-1701BLB/HLS-1701B Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below :
The bath has strong anti-shrinkage and anti-pollution ability.
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
Ideal for high demand for salt spray industry, such as pipe trench, auto chassis parts, castings
Coating fullness of good, better substrate hiding .
Main ingredients :
|
Curing agent: totally enclosed multi-isocyanates
|
|
Solvent: alcohol ether
|
|
Neutralizing agent: organic acid
|
|
Additives: surface active agent, prevent shrinkage cavity agent
|
|
Matrix resin: polyurethane modified epoxy resin
|
Product film performance
| Project | Indicator | Test standard | |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 72 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 48 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 1000 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Construction equipment :
Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment:
Electrophoresis tank
Circulation devices (including filter, fill the paint device)
DI water equipment
DC power supply and the power supply unit
Anode box (tube) and circulation device
Ultrafiltration device
Cleaning devices
Heat exchanging equipment
Curing device
Storage, packaging and transportation :
This product is a water-borne industrial coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L Plastic barrel; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products, including paste resin, emulsions and additives should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5～35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.