|Application Field:||Other Parts Of The Car||Performance:||Better Substrate Hiding|
|Cooperation Case:||Yuancheng，DONGFENG MOTOR||Main Ingredients:||Organic Acid ; Alcohol Ether|
black e coat,
black edp coating
Black electrophoretic paint for other parts of the car like Plate spring
Product Introduction :
HL-1607LB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below:
|The bath has strong anti-shrink age andanti-pollutionability.||Coating fullness of good,better sub strate hiding. |
|Strong anti-corrosion properties, good salt spray resistance workpiece edge.||The appearance of the coating is flat, delicate, smooth, uniform high gloss.|
Matrix resin: Acrylic modified epoxy resin
Pigment: carbon black, kaolin, antirust pigment
Additives:surface active agent, prevent shrinkage cavity agent
Product film performance:
|Appearance||Normal / abnormal||Normal||Ocular estimate|
|Cup drawing||mm ,≥||6||GB/T 9753|
|Water resistance||h,(23±2)℃,≥||240||GB/T 1733|
|Acid resistance||h,(50g/L H2SO4),≥||72||GB/T 9274|
|Alkali resistance||h,(50g/L NaOH),≥||72||GB/T 9274|
|*Salt spray resistance||h,(film thickness ≥ 20μm) ,≥||1000||GB/T 1771|
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.