Car doors black electrophoresis paint for Passenger cars and commercial vehicles

Certification
China HLS Coatings (Shanghai)Co.Ltd certification
China HLS Coatings (Shanghai)Co.Ltd certification
I'm Online Chat Now

Car doors black electrophoresis paint for Passenger cars and commercial vehicles

Car doors black electrophoresis paint for Passenger cars and commercial vehicles
Car doors black electrophoresis paint for Passenger cars and commercial vehicles

Large Image :  Car doors black electrophoresis paint for Passenger cars and commercial vehicles

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HLS-1701BLB/HLS-1701B
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day

Car doors black electrophoresis paint for Passenger cars and commercial vehicles

Description
Main Ingredients: Antirust Pigment Application Field: Car Covers
Performance: Excellent Adhesion Cooperation Case: SAIC Motor
High Light:

black edp coating

,

black epoxy coating

Car doors black electrophoresis paint for Passenger cars and commercial vehicles

 

Product Introduction :

 

 

HLS-1701BLB/HLS-1701B Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.

 

It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.

 

 

This product features shown below: 

 

 

Coating fullness of good, better substrate hiding .
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
The appearance of the coating is flat, delicate, smooth.
Good stability of bath can adaptable for a longer updating cycle. 
Excellent leveling coating,good bonding force and compatibility with plastic powder.

 

 

Filling tank proportion and method

 

Ripening conditions

Sample quantity 3000~4000g
Container 4L (Diameter 16cm)
Tank temperature 28-30 ℃
Time 24~48Hr
Mixed conditions impeller diameter 8cm (speed 200rpm)

 


(2) Coating conditions

Experimental panel phosphated cold-rolled steel plate
Tank temperature 28-35℃
Pole ratio A/C = 1/2 ~ 1/4
Distance of electrodes 15cm
ED time For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions (175-185)℃×(20-30)min (Keeping temperature of parts coated)

 


 

Product film performance

 

Project Indicator Test standard
Appearance Normal / abnormal Normal Ocular estimate
Hardness 2H GB/T 6739
Cup drawing mm ,≥ 6 GB/T 9753
Adhesion Level 0 GB/T 9286
Flexibility mm 1 GB/T 1731
Impact kg·cm 50 GB/T 1732
Gloss 60 50-80 GB/T 9754
Water resistance h,(23±2)℃,≥ 240 GB/T 1733
Acid resistance h,(50g/L H2SO4),≥ 72 GB/T 9274
Alkali resistance h,(50g/L NaOH),≥ 48 GB/T 9274
*Salt spray resistanc​e h,(film thickness ≥ 20μm) ,≥ 1000 GB/T 1771

* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.

 

Customer production site:

 

Car doors black electrophoresis paint for Passenger cars and commercial vehicles 0

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)