Ultra Low Temperature Electrophoretic Coating Anti Corrosion Coating For Car
Product Details
| Application Field: | Car Shock | Cooperation Case: | ZHONGDING |
|---|---|---|---|
| Performance: | Low Temperature | Main Ingredients: | Titanium Pigment; Antirust Pigment |
| Highlight |
cathodic electrocoating,car body coating |
||
Product Description
Solution for the Car shock electrophoresis paint.
Product Introduction
OHT-825/OHT-825 Ultra Low temperature Black Cationic Epoxy Electrocoat, is HLS Paint (Shanghai) Co., Ltd. the ninth generation of independent research and development of electrophoretic coating. The lead, cadmium, chromium, mercury and other heavy metals, two-component aqueous dispersion resin. At the same time, inherited the characteristics of several generations of product quality, OHT-825 on galvanized steel sheet has good adaptability, almost at the bottom of all the metal material coating, such as: cold rolled steel, galvanized steel, aluminum, stainless steel plate, rubber parts, zinc and aluminum alloy plate, such as applicable
This product features shown below:
Particularly suitable for high temperature baking of the workpiece, in particular, rubber and metal binding parts and zinc aluminum alloy material.
Ultra low temperature curing completely green does not contain heavy metals, in conformity with the European ROHS, the instruction of PAHs, reach, fohs, can save about 60% of the energy consumption, is the national government absolute attention and support energy-saving emission reduction requirements of the project, the state and the enterprises and the people.
Main ingredients
Additives: surface active agent, prevent shrinkage cavity agent
Pigment: carbon black, kaolin, antirust pigment
Solvent: alcohol ether
Product quality data
| Project | Technical data | Test standard | ||
| Resin (OHT-825) |
Black Paste (OHT-825) | |||
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Appearance | —— | Milky white liquid | Black viscous liquid,no agglomeration | Visual |
| Conductivity | 25℃, μs/cm | 1400±500 | —— | HG/T 3334 |
| Storage stability | No stratified state, and there were no obvious difference compared to before storage |
In 5-35 ℃ temperature 1 year | ||
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Filling tank proportion and method
⑴ Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-35℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(130-140)℃×(20-30)min (Keeping temperature of parts coated)
Product film performance
| Project | Indicator | Test standard | |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 7 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 60-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 48 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 48 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 800 | JIS K 5600-7-1 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Construction equipment
Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment:
Electrophoresis tank
Circulation devices (including filter, fill the paint device)
DI water equipment
DC power supply and the power supply unit
Anode box (tube) and circulation device
Ultrafiltration device
Cleaning devices
Heat exchanging equipment
Curing device
Customers in the electric vehicle industry
|
|
|
Product Highlights
Solution for the Car shock electrophoresis paint. Product Introduction OHT-825/OHT-825 Ultra Low temperature Black Cationic Epoxy Electrocoat, is HLS Paint (Shanghai) Co., Ltd. the ninth generation of independent research and development of electrophoretic coating. The lead, cadmium, chromium, ...
High Throwing Power E Coating Car Body Paint Does Not Contain Heavy Metal
Solution for the Passenger car electrophoresis paint http://haolisen.com Product Introduction : HR-7001LB/HR-7010 Gray Cationic Epoxy Electrocoat for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS ...
ISO9001 High Weatherability Electrophoretic Paint For Commercial Vehicles
High weatherability electrophoretic paint for Commercial vehicles Product Introduction : HR-7001LB/HR-7010 Gray Cationic Epoxy Electrocoat for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS International ...
Gray Cationic Epoxy E Coat Paint , Electrolysis Anti Rust Paint For Cars
Solution for the bus electrophoresis paint Product Introduction HLS-5701LB/HLS-5750 Gray Cationic Epoxy Electrocoat for auto is the 7th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS International Chemical Industry Group. ...
Radiator White Epoxy Acrylic Cathodic Electrodeposition Paint Resistance To Yellowing
Solution for radiator electrodeposition coating Product Introduction : HS-5500LB/HS-5500 White epoxy acrylic cathodic electrophoretic coating for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. and get the national invention patent and ...
Please use our online inquiry contact form below if you have any questions, our team will get back to you as soon as possible.