High Performance Electrophoresis Paint , Electrocoating Anti Rust Coating For Car Wipers
Product Details
| Cooperation Case: | VALEO，SHB GROUP | Application Field: | Car Wipers |
|---|---|---|---|
| Product Name: | ED Paint For Other Parts Of The Car | Main Ingredients: | Organic Acid ;antirust Pigment |
| Highlight |
cathodic electrocoating,car paint coating |
||
Product Description
Solution for the Car wipers electrophoresis paint.
Product Introduction
HLS-1701ELB/HLS-1701EG Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.
This product features shown below:
1.Good stability of bath can adaptable for a longer updating cycle.
2.Strong anti-corrosion properties, good salt spray resistance workpiece edge.
The main component Matrix resin:
| Solvent: alcohol ether | Additives: surface active agent, prevent shrinkage cavity agent |
| Pigment: Titanium pigment, carbon black, kaolin, antirust pigment | |
Product quality data
| Project | Technical data | Test standard | ||
| Resin (HLS-1701ELB) |
Black Paste (HLS-1701EG) | |||
| Appearance | —— | Milky white liquid | Black viscous liquid,no agglomeration | Visual |
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1400±600 | —— | HG/T 3334 |
| Storage stability | No stratified state, and there were no obvious difference compared to before storage |
In 5-35 ℃ temperature 1 year | ||
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Filling tank proportion and method
⑴ Bath preparation
Ratio:
Resin 1200.00
Paste 200.00
DI water 2000.00
Total 3400.00
⑵ Ripening conditions
Sample quantity: 3000～5000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 30-36℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(165-185)℃×(20-30)min (Keeping temperature of parts coated)
Bath on site management project
Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:
| Classification | Project | Control Data | Testing frequency | |
| New bath | Anolyte | |||
| Electrophoresis tank | Ratio | 1:6 | -- | |
| Ripening time | 24-48 | -- | ||
| Solid ( 120 ℃ /1h ,% ) | 14±4 | -- | once a day | |
| PH | 5.6-6.2 | 2.0-3.5 | once a day | |
| Conductivity ( μs/cm ) | 1200±400 | 2000±1000 | once a day | |
| P/B | 0.08-0.15 | once a week | ||
| L panel | Smooth horizontal plane and vertical plane without obvious differences | once a week | ||
| Solvent content (%) | 0.5-1.2 | once a week | ||
| Liquid level Fall head (cm ) | 10-15 | once a day | ||
| ED voltage( V ) | 0-300 | once a day | ||
| Break voltage ( V ) | ≥320 | once a week | ||
| Bath temperature ( ℃ ) | 30-36 | once a day | ||
| ED time( S ) | 60-180 | once a day | ||
| UF － 1 Tank | Solid content (%) | ≤2.0 | once a day | |
| UF － 2 Tank | Solid content (%) | ≤0.8 | once a day | |
| Baking furnace | Provisions furnace temperature( ℃ ) | 170-190 | once a day | |
| Curing conditions | Drying temperature | (165-185)℃×(20-30)min (With content holding time) |
once a day | |
HLS's service objects:
|
|
Product Highlights
Solution for the Car wipers electrophoresis paint. Product Introduction HLS-1701ELB/HLS-1701EG Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic ...
High Throwing Power E Coating Car Body Paint Does Not Contain Heavy Metal
Solution for the Passenger car electrophoresis paint http://haolisen.com Product Introduction : HR-7001LB/HR-7010 Gray Cationic Epoxy Electrocoat for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS ...
ISO9001 High Weatherability Electrophoretic Paint For Commercial Vehicles
High weatherability electrophoretic paint for Commercial vehicles Product Introduction : HR-7001LB/HR-7010 Gray Cationic Epoxy Electrocoat for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS International ...
Gray Cationic Epoxy E Coat Paint , Electrolysis Anti Rust Paint For Cars
Solution for the bus electrophoresis paint Product Introduction HLS-5701LB/HLS-5750 Gray Cationic Epoxy Electrocoat for auto is the 7th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS International Chemical Industry Group. ...
Radiator White Epoxy Acrylic Cathodic Electrodeposition Paint Resistance To Yellowing
Solution for radiator electrodeposition coating Product Introduction : HS-5500LB/HS-5500 White epoxy acrylic cathodic electrophoretic coating for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. and get the national invention patent and ...
Please use our online inquiry contact form below if you have any questions, our team will get back to you as soon as possible.