Non Hazardous E Coating Car Body With Fully Enclosed Multi Isocyanate Curing Agent

Non Hazardous E Coating Car Body With Fully Enclosed Multi Isocyanate Curing Agent
Non Hazardous E Coating Car Body With Fully Enclosed Multi Isocyanate Curing Agent

Large Image :  Non Hazardous E Coating Car Body With Fully Enclosed Multi Isocyanate Curing Agent

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HL-1607LB/HLS-1701A
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day

Non Hazardous E Coating Car Body With Fully Enclosed Multi Isocyanate Curing Agent

Description
Application Field: Car Seat Color: Black
Main Ingredients: Titanium Pigment;carbon Black, Kaolin Cooperation Case: SAIC Motor
High Light:

cathodic electrocoating

,

car paint coating

Solution for the Car seat electrophoresis paint.

 

Product Introduction

 

HL-1607LB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.

 

This product features shown below: 

 

Good stability of bath can adaptable for a longer updating cycle. 

Strong anti-corrosion properties,good salt spray resistance workpiece edge. 

 

Main ingredients

 

 

Curing agent: Fully enclosed multi isocyanate

 

Additives: surface active agent, prevent shrinkage cavity agent

 

 

Filling tank proportion and method

 

⑴ Bath preparation

Ratio:

Resin                      800.00-1200.00

Paste                                    200.00

DI water                              2000.00


Total                                    3400.00

⑵ Ripening conditions

Sample quantity: 3000~3400g
Container: 4L (Diameter 16cm)

Tank temperature: 28-30 ℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)


(3) Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 28-35℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions:(175-185)℃×(20-30)min (Keeping temperature of parts coated)


 

Storage, packaging and transportation

 

This product is a water-borne industrial coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L Plastic barrel; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products, including paste resin, emulsions and additives should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5~35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.

 

Customer production site

 

Non Hazardous E Coating Car Body With Fully Enclosed Multi Isocyanate Curing Agent 0

 

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Fax: 86-021-69122952

Send your inquiry directly to us (0 / 3000)