Payment & Shipping Terms:
|Color:||Grey||Application Field:||Passenger Car|
|Performance:||High Throwing Power||Cooperation Case:||GEELY AUTO|
car paint coating
Solution for the Passenger car electrophoresis paint
Product Introduction :
HR-7001LB/HR-7010 Gray Cationic Epoxy Electrocoat for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS International Chemical Industry Group. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc
This product features shown below:
The appearance of the coating is flat, delicate, smooth.
Good stability of bath can adaptable for a longer updating cycle.
The bath has strong anti-shrinkage and anti-pollution ability.
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
High throwing power, internal and external uniformity.
Coating fullness of good, better substrate hiding .
suitable for auto body industry, such as cars, SUV and other models
The main component :
|Pigment: Titanium pigment, carbon black, kaolin, antirust pigment||Additives: surface active agent, prevent shrinkage cavity agent, anti-yellowing agent.|
|Solvent: alcohol ether||Neutralizing agent: organic acid|
|Curing agent: totally enclosed multi-isocyanates||Matrix resin: polyurethane modified epoxy resin|
The main supplier:
|Bisphenol A epoxy resins||Formosa Plastic Group / Kukdo / Dow Chemical|
|Amine hardendner||INTERSCAN / Huntsman Corporation|
|Carbon black||Cabot Corporation|
Product film performance :
|Appearance||Normal / Abnormal||Normal||Ocular estimate|
|Cup drawing||mm,≥||6||GB/T 9753|
|Water resistance||h,(23±2)℃ ≥||240||GB/T 1733|
|Acid resistance||h(0.05N H2SO4) ≥||72||GB/T 9274|
|Alkali resistance||h(0.1N NaOH) ≥||72||GB/T 9274|
|Gasoline resistance||93#,24h||No bubbles, no wrinkles, no rust, no shedding||GB/T 9274|
|Interlayer adhesion||≤level||1||GB/T 9286|
|*Salt spray resistance||film thickness ≥ 20μm||1000||GB/T 1771|
|Stone strike resistance||level ≤||3.0||Q/DFLCM 5466|
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.