Payment & Shipping Terms:
|Application Field:||Elevator Parts||Performance:||Not Fade|
|Cooperation Case:||HITACHI，CANNY ELEVATOR||Main Ingredients:||Antirust Pigment,kaolin|
black e coat,
black epoxy coating
Black electrophoretic paint for elevator and the parts
Product Introduction :
HLS-1701ALB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below:
1,Good stability of bath can adaptable for a longer updating cycle.
2,Have excellent corrosion resistance and weathering resistance, especially suitable for the bottom surface of a painting；
3,The appearance of the coating is flat, delicate, smooth, uniform high gloss.
Additives: surface active agent, prevent shrinkage cavity agent ,
Resin: polyurethane modified epoxy resin ,
Curing agent: totally enclosed multi-isocyanates .
Product quality data:
|Project||Technical data||Test standard|
|Black Paste (HLS-1701A)|
|Conductivity||25℃, μs/cm||1400±600||——||HG/T 3334|
|Appearance||——||Milky white liquid||Black viscous liquid,no agglomeration||Visual|
No stratified state, and there were no obvious difference compared to before storage
|In 5-35 ℃ temperature 1 year|
Filling tank proportion and method:
⑴ Bath preparation
DI water 2000.00
⑵ Ripening conditions
Sample quantity: 3000～5000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 30-36℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(165-185)℃×(20-30)min (Keeping temperature of parts coated)