Solution of electrophoretic paint for rotary tiller
Product Introduction :
HL-1607LB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below:
1,Strong anti-corrosion properties, good salt spray resistance workpiece edge.
2,The appearance of the coating is flat, delicate, smooth, uniform high gloss.
3,Coating fullness of good,better sub strate hiding.
4,The bath has strong anti-shrink age andanti-pollutionability.
|Matrix resin: Acrylic modified epoxy resin||
Pigment: carbon black, kaolin, antirust pigment
Additives:surface active agent, prevent shrinkage cavity agent
Product quality data :
|Project||Technical data||Test standard|
|Black Paste (HLS-1701A)|
|Appearance||——||Milky white liquid||Black viscous liquid,no agglomeration||Visual|
|Conductivity||25℃, μs/cm||1400±600||——||HG/T 3334|
No stratified state, and there were no obvious difference compared to before storage
|In 5-35 ℃ temperature 6 months|
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Filling tank proportion and method:
⑴ Bath preparation
DI water 2000.00
⑵ Ripening conditions
Sample quantity: 3000～3400g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-35℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(175-185)℃×(20-30)min (Keeping temperature of parts coated)
Storage, packaging and transportation:
This product is a water-borne industrial coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L Plastic barrel; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products, including paste resin, emulsions and additives should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5～35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.