High Performance Electrophoresis Paint , Electrocoating Anti Rust Coating For Car Wipers

China HLS Coatings (Shanghai)Co.Ltd certification
China HLS Coatings (Shanghai)Co.Ltd certification
I'm Online Chat Now

High Performance Electrophoresis Paint , Electrocoating Anti Rust Coating For Car Wipers

High Performance Electrophoresis Paint , Electrocoating Anti Rust Coating For Car Wipers
High Performance Electrophoresis Paint , Electrocoating Anti Rust Coating For Car Wipers

Large Image :  High Performance Electrophoresis Paint , Electrocoating Anti Rust Coating For Car Wipers

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HLS-1701ELB/HLS-1701EG
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day
Detailed Product Description
Cooperation Case: VALEO,SHB GROUP Application Field: Car Wipers
Product Name: ED Paint For Other Parts Of The Car Main Ingredients: Organic Acid ;antirust Pigment
High Light:

cathodic electrocoating

,

car paint coating

Solution for the Car wipers electrophoresis paint.

 

Product Introduction

 

HLS-1701ELB/HLS-1701EG Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.

 

This product features shown below:

 

1.Good stability of bath can adaptable for a longer updating cycle. 

 

2.Strong anti-corrosion properties, good salt spray resistance workpiece edge. 

 

The main component Matrix resin:

 

Solvent: alcohol ether Additives: surface active agent, prevent shrinkage cavity agent
Pigment: Titanium pigment, carbon black, kaolin, antirust pigment

 

Product quality data

 

Project Technical data Test standard
Resin
(HLS-1701ELB)
              Black Paste               (HLS-1701EG)
Appearance —— Milky white liquid Black viscous liquid,no agglomeration Visual
pH 25℃ 6.0±1.0 —— GB/T 9724
Conductivity 25℃, μs/cm 1400±600 —— HG/T 3334
Storage stability
No stratified state, and there were no obvious difference compared to before storage
In 5-35 ℃ temperature 1 year

Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution

 

Filling tank proportion and method

 

⑴ Bath preparation

Ratio:

Resin                                                 1200.00

Paste                                                   200.00

DI water                                             2000.00


Total                                                  3400.00

⑵ Ripening conditions

Sample quantity: 3000~5000g
Container: 5L (Diameter 16cm)

Tank temperature:28-30 ℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)


(3) Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 30-36℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions:(165-185)℃×(20-30)min (Keeping temperature of parts coated)


 

Bath on site management project

 

Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:

 

Classification Project Control Data Testing frequency
New bath Anolyte
Electrophoresis tank Ratio 1:6 --  
Ripening time 24-48 --  
Solid ( 120 ℃ /1h ,% ) 14±4 -- once a day
PH 5.6-6.2 2.0-3.5 once a day
Conductivity ( μs/cm ) 1200±400 2000±1000 once a day
P/B 0.08-0.15 once a week
L panel Smooth horizontal plane and vertical plane without obvious differences once a week
Solvent content (%) 0.5-1.2 once a week
Liquid level Fall head (cm ) 10-15 once a day
ED voltage( V ) 0-300 once a day
Break voltage ( V ) ≥320 once a week
Bath temperature ( ℃ ) 30-36 once a day
ED time( S ) 60-180 once a day
UF - 1 Tank Solid content (%) ≤2.0 once a day
UF - 2 Tank Solid content (%) ≤0.8 once a day
Baking furnace Provisions furnace temperature( ℃ ) 170-190 once a day
Curing conditions Drying temperature
(165-185)℃×(20-30)min (With content holding time)
once a day

 

 

HLS's service objects​:

 

High Performance Electrophoresis Paint , Electrocoating Anti Rust Coating For Car Wipers 0 High Performance Electrophoresis Paint , Electrocoating Anti Rust Coating For Car Wipers 1

 

 

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)