Product Details:
|
| Performance: | Good Stability | Cooperation Case: | JOHN DEERE |
|---|---|---|---|
| Main Ingredients: | Carbon Black, Kaolin | Application Field: | Fertilizer Machine |
| High Light: | cationic epoxy electrocoat,electro coating |
||
Solution for application of electrophoresis paint of fertilizer machine
Product Introduction :
HLS-1701BLB/HLS-1701B Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below :
1, Good stability of bath can adaptable for a longer updating cycle.
2, Coating fullness of good, better substrate hiding .
3, Strong anti-corrosion properties, good salt spray resistance workpiece edge.
Main ingredients :
|
Pigment: Titanium pigment, carbon black, kaolin, antirust pigment
|
Additives: surface active agent, prevent shrinkage cavity agent |
|
Solvent: alcohol ether
|
Neutralizing agent: organic acid |
|
Curing agent: totally enclosed multi-isocyanates
|
Matrix resin: polyurethane modified epoxy resin |
Bath on site management project:
Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:
| Classification | Project | Control Data | Testing frequency | |
| New bath | Anolyte | |||
| Electrophoresis tank | Ratio | 1:6 | -- | |
| Ripening time | 24-48 | -- | ||
| Solid ( 120 ℃ /1h ,% ) | 14±4 | -- | once a day | |
| PH | 5.6-6.2 | 2.0-3.5 | once a day | |
| Conductivity ( μs/cm ) | 1200±400 | 2000±1000 | once a day | |
| P/B | 0.08-0.15 | once a week | ||
| Solvent content (%) | 0.5-1.2 | once a week | ||
| Liquid level Fall head (cm ) | 10-15 | once a day | ||
| ED voltage( V ) | 0-300 | once a day | ||
| Break voltage ( V ) | ≥320 | once a week | ||
| Bath temperature ( ℃ ) | 30-36 | once a day | ||
| ED time( S ) | 60~180 | once a day | ||
| UF － 1 Tank | Solid content (%) | ≤2.0 | once a day | |
| UF － 2 Tank | Solid content (%) | ≤0.8 | once a day | |
| Baking furnace | Provisions furnace temperature( ℃ ) | 185-195 | once a day | |
| Curing conditions | Drying temperature | (180-190) ℃ ×(15-20)min (With content holding time) |
once a day | |
Construction equipment :
Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment:
Electrophoresis tank
Circulation devices (including filter, fill the paint device)
DI water equipment
DC power supply and the power supply unit
Anode box (tube) and circulation device
Ultrafiltration device
Cleaning devices
Heat exchanging equipment
Curing device