Non Toxic Cationic Electrolysis Painting Black Epoxy Coating Salt Spray Resistance

Non Toxic Cationic Electrolysis Painting Black Epoxy Coating Salt Spray Resistance
Non Toxic Cationic Electrolysis Painting Black Epoxy Coating Salt Spray Resistance
video play

Large Image :  Non Toxic Cationic Electrolysis Painting Black Epoxy Coating Salt Spray Resistance

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HLS-1701B/HLS-1701B
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day
Detailed Product Description
Performance: Good Anticorrosive Cooperation Case: SANY,LION CHINA
Main Ingredients: Alcohol Ether ;Titanium Pigment Application Field: Engineering Mechanical
High Light:

black edp coating

,

black epoxy coating

Engineering mechanical or the parts for the black electrophoretic paint

 

Product Introduction

 

1.HLS-1701BLB/HLS-1701B Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.

2.It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.

 

This product features shown below: 

 

Good stability of bath can adaptable for a longer updating cycle. Coating fullness of good, better substrate hiding . Strong anti-corrosion properties, good salt spray resistance workpiece edge. 

 

 

Main ingredients

 

Additives: surface active agent, prevent shrinkage cavity agent
Solvent: alcohol ether Neutralizing agent: organic acid

 

 

 

 

Filling tank proportion and method

 

Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 30-36℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions:(180-190)℃×(20-30)min (Keeping temperature of parts coated)


 

Product film performance

 

Project Indicator Test standard
Appearance Normal / abnormal Normal Ocular estimate
Hardness 2H GB/T 6739
Cup drawing mm ,≥ 6 GB/T 9753
Adhesion Level 0 GB/T 9286
Flexibility mm 1 GB/T 1731
Impact kg·cm 50 GB/T 1732
Gloss 60 50-80 GB/T 9754
Water resistance h,(23±2)℃,≥ 240 GB/T 1733
Acid resistance h,(50g/L H2SO4),≥ 72 GB/T 9274
Alkali resistance h,(50g/L NaOH),≥ 48 GB/T 9274
*Salt spray resistanc​e h,(film thickness ≥ 20μm) ,≥ 1000 GB/T 1771

* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.


 

Customers in the engineering machinery

 

Non Toxic Cationic Electrolysis Painting Black Epoxy Coating Salt Spray Resistance 0

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)