Solution for flange electrophoresis paint
①,Good stability of bath can adaptable for a longer updating cycle.
②,Strong anti-corrosion properties.
③,Coating fullness of good, better substrate hiding
|
Matrix resin:acrylic modified epoxy resin
|
Solvent:alcohol ether |
|
Curing agent:totally enclosed multi-isocyanates
|
Pigment:Titanium pigment, Organic pigment, kaolin, antirust pigment |
Product film performance :
| Project | Indicator | Test standard | |
| Appearance | Normal / Abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm,≥ | 6 | GB/T 9753 |
| Adhesion | level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | Kg.cm | 50 | GB/T 1732 |
| Gloss | 60° | 40-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃ ≥ | 240 | GB/T 1733 |
| Acid resistance | h(0.05N H2SO4) ≥ | 48 | GB/T 9274 |
| Alkali resistance | h(0.1N NaOH) ≥ | 48 | GB/T 9274 |
| *Salt spray resistance | film thickness ≥ 25μm | 500 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Construction equipment :
Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment:
|
Electrophoresis tank
|
Circulation devices (including filter, fill the paint device) | DI water equipment |
|
DC power supply and the power supply unit
|
Anode box (tube) and circulation device | Ultrafiltration device |
|
Cleaning devices
|
Heat exchanging equipment | Curing device |
Customers in the flange industry :
Fax: 86-021-69122952