Product Introduction :
AED-2000LB/AED-2000 White anodic electrophoretic coatings for auto is the 1th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd..
This coating has excellent weather resistance, smooth appearance.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin. The coating that does not contain tin element meet the latest environ-mental regulations of European Union, North America, Japan and other requirements in advance, which is the inevitable trend of future environ-mental coating and low cost; meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal,
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.
This product features shown below:
Have excellent weather resistance
Excellent yellowing resistance
Matrix resin: Acrylic modified epoxy resin
Curing agent: Fully enclosed multi isocyanate
Additives: surface active agent, prevent shrinkage cavity agent
Ngan: titanium dioxide, kaolin
Product quality data:
|Project||Technical data||Test standard|
|White Paste (AED-2000)|
|Conductivity||25℃, μs/cm||800±500||——||HG/T 3334|
|Appearance||——||Milky white liquid||White viscous liquid,no agglomeration||Visual|
No stratified state, and there were no obvious difference compared to before storage
|In 5-35 ℃ temperature 1 year|
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Product film performance:
|Appearance||Normal / abnormal||Normal||Ocular estimate|
|Cup drawing||mm ,≥||6||GB/T 9753|
|Acid resistance||h,(50g/L H2SO4),≥||20||GB/T 9274|
|Alkali resistance||h,(50g/L NaOH),≥||24||GB/T 9274|
|*Salt spray resistance||h,(film thickness ≥ 20μm) ,≥||600||GB/T 14522|
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.