Anti Shrinkage Black E Coat , Cathodic Electrocoating For Motorcycle Parts

China HLS Coatings (Shanghai)Co.Ltd certification
China HLS Coatings (Shanghai)Co.Ltd certification
I'm Online Chat Now

Anti Shrinkage Black E Coat , Cathodic Electrocoating For Motorcycle Parts

Anti Shrinkage  Black E Coat , Cathodic Electrocoating For Motorcycle Parts
Anti Shrinkage  Black E Coat , Cathodic Electrocoating For Motorcycle Parts Anti Shrinkage  Black E Coat , Cathodic Electrocoating For Motorcycle Parts Anti Shrinkage  Black E Coat , Cathodic Electrocoating For Motorcycle Parts

Large Image :  Anti Shrinkage Black E Coat , Cathodic Electrocoating For Motorcycle Parts

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HR-4000BLB/HR-6000
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day
Detailed Product Description
Application Field: Motorcycle Main Ingredients: Carbon Black, Antirust Pigment
Performance: Film Is Bright Cooperation Case: DAYUN,ZONGSHEN,LONCIN
High Light:

black e coat

,

black epoxy coating

Black electrophoresis paint for the Motorcycle and the parts

 

Product Introduction

 

HR-4000BLB/HR-6000 the bottom of one black cathode electrophoretic coating, is HLS Paint (Shanghai) Co., Ltd., the eighth generation of independent research and development of electrophoretic coating. This coating by epoxy acrylate modified, the film also has excellent corrosion resistance and weatherability, smooth appearance and full, suitable as a base topcoat system. In addition, the lead, cadmium, chromium, mercury and other heavy metals, two-component, water dispersible resin, at the same time, previous generations of the product characteristics, have good adaptability to the galvanized steel, almost can be applied to all metal coating, such as: cold hot rolled steel, galvanized steel, aluminum, zinc Aluminum Alloy plate, stainless steel plate.

 

This product features shown below: 

 

The appearance of the coating is flat, delicate, smooth. 

Good stability of bath can adaptable for a longer updating cycle. 

 

Main ingredients

 

Matrix resin: Acrylic modified epoxy resin

Curing agent: Fully enclosed multi isocyanate

 

Product quality data

 

Project Technical data Test standard
Resin
(HR-4000LB)
Black Paste (HR-6000)
Conductivity 25℃, μs/cm 1000±500 —— HG/T 3334
pH 25℃ 6.0±1.0 —— GB/T 9724
Appearance —— Milky white liquid Black viscous liquid,no agglomeration Visual
Storage stability
No stratified state, and there were no obvious difference compared to before storage
In 5-35 ℃ temperature 1 year

Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution

 

Filling tank proportion and method

 

⑴ Bath preparation

Ratio:

Resin 1050.00-1400.00

Paste 175.00

NHF-01 2.00

DI water 1785.00


 

 

Bath on site management project

 

Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:

 

Classification Project Control Data Testing frequency
New bath Anolyte
Electrophoresis tank Ratio 1:(6-8) --  
Ripening time 24-48 --  
Solid ( 120 ℃ /1h ,% ) 15±5 -- once a day
PH 5.4-6.0 2.0-3.5 once a day
Conductivity ( μs/cm ) 1000±500 1400±900 once a day
P/B 0.08-0.15 once a week
L panel Smooth horizontal plane and vertical plane without obvious differences once a week
Solvent content (%) 0.5-1.8 once a week
Liquid level Fall head (cm ) 10-15 once a day
ED voltage( V ) 0-300 once a day
Break voltage ( V ) ≥350 once a week
Bath temperature ( ℃ ) 28-35 once a day
ED time( S ) 60~180 once a day
UF - 1 Tank Solid content (%) ≤2.0 once a day
UF - 2 Tank Solid content (%) ≤0.8 once a day
Baking furnace Provisions furnace temperature( ℃ ) 170-190 once a day
Curing conditions Drying temperature
(165-185)℃×(20-30)min (With content holding time)
once a day

 

 

Storage, packaging and transportation

 

This product is a water-borne industrial coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L Plastic barrel; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products, including paste resin, emulsions and additives should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5~35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.
 

Customers in the motorcycle  industry

 

Anti Shrinkage  Black E Coat , Cathodic Electrocoating For Motorcycle Parts 0

 

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)