High throwing power penetration electrophoresis paint for passenger car body
Product Introduction :
HR-7001LB/HR-7010 Gray Cationic Epoxy Electrocoat for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS International Chemical Industry Group.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc
This product features shown below:
1,The appearance of the coating is flat, delicate, smooth.
2,The bath has strong anti-shrinkage and anti-pollution ability.
3,High throwing power, internal and external uniformity.
4,suitable for auto body industry, such as cars, SUV and other models
The main supplier:
| Material name | Supplier |
| Bisphenol A epoxy resins | Formosa Plastic Group / Kukdo / Dow Chemical |
| Polyisocyanates | Bayer |
| Amine hardendner | INTERSCAN / Huntsman Corporation |
| Titanium pigment | DuPont |
| Kaolin | Neuburg |
| Carbon black | Cabot Corporation |
Product film performance :
| Project | Indicator | Test standard | |
| Appearance | Normal / Abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm,≥ | 6 | GB/T 9753 |
| Adhesion | level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | Kg.cm | 50 | GB/T 1732 |
| Gloss | 60° | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃ ≥ | 240 | GB/T 1733 |
| Acid resistance | h(0.05N H2SO4) ≥ | 72 | GB/T 9274 |
| Alkali resistance | h(0.1N NaOH) ≥ | 72 | GB/T 9274 |
| Gasoline resistance | 93#,24h | No bubbles, no wrinkles, no rust, no shedding | GB/T 9274 |
| Interlayer adhesion | ≤level | 1 | GB/T 9286 |
| *Salt spray resistance | film thickness ≥ 20μm | 1000 | GB/T 1771 |
| Stone strike resistance | level ≤ | 3.0 | Q/DFLCM 5466 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Specification statement:
This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.
If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now
Customer production site :
Fax: 86-021-69122952