No Lead No Tin Ed Black Coating , Cataphoretic Coating For Rotary Tiller

Good quality Cathodic Electrodeposition Paint for sales
Good quality Cathodic Electrodeposition Paint for sales
I'm Online Chat Now

No Lead No Tin Ed Black Coating , Cataphoretic Coating For Rotary Tiller

China No Lead No Tin Ed Black Coating , Cataphoretic Coating For Rotary Tiller supplier

Large Image :  No Lead No Tin Ed Black Coating , Cataphoretic Coating For Rotary Tiller

Product Details:

Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HL-1607LB/HLS-1701A

Payment & Shipping Terms:

Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day
Contact Now
Detailed Product Description
Application Field: Other Parts Of The Car Performance: Better Substrate Hiding
Cooperation Case: Yuancheng,DONGFENG MOTOR Main Ingredients: Organic Acid ; Alcohol Ether

Solution of electrophoretic paint for rotary tiller

 

Product Introduction :

 

HL-1607LB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.

 

It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal

 

such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.


 

This product features shown below: 

 

1,Strong anti-corrosion properties, good salt spray resistance workpiece edge.

 

2,The appearance of the coating is flat, delicate, smooth, uniform high gloss.

 

3,Coating fullness of good,better sub strate hiding.

 

4,The bath has strong anti-shrink age andanti-pollutionability.


Main ingredients:

 

Matrix resin: Acrylic modified epoxy resin

 

 

Pigment: carbon black, kaolin, antirust pigment

 

 

Additives:surface active agent, prevent shrinkage cavity agent

 

 

 

Product quality data :

 

Project Technical data Test standard
Resin
(HL-1607 LB)
Black Paste (HLS-1701A)
Appearance —— Milky white liquid Black viscous liquid,no agglomeration Visual
pH 25℃ 6.0±1.0 —— GB/T 9724
Conductivity 25℃, μs/cm 1400±600 —— HG/T 3334
Storage stability
No stratified state, and there were no obvious difference compared to before storage
In 5-35 ℃ temperature 6 months

 

Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution

 

Filling tank proportion and method:

 

⑴ Bath preparation

Ratio:

Resin                                                  800.00-1200.00

Paste                                                                200.00

DI water                                                          2000.00


Total                                                               3400.00

⑵ Ripening conditions

Sample quantity: 3000~3400g
Container: 5L (Diameter 16cm)

Tank temperature:28-30 ℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)


(3) Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 28-35℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions:(175-185)℃×(20-30)min (Keeping temperature of parts coated)


Storage, packaging and transportation:

 

This product is a water-borne industrial coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L Plastic barrel; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products, including paste resin, emulsions and additives should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5~35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.


If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now


 

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)