Product Details:
|
| Main Ingredients: | Alcohol Ether ; Carbon Black | Performance: | Film Fastening |
|---|---|---|---|
| Application Field: | Colorful Products | Cooperation Case: | TORIN TOOLS |
| High Light: | electrodeposition paint,e coated steel |
||
High weatherability colorful electrophoretic paint with Uv radiation resiistance
HR-4000BLB Epoxy acrylic Color Cationic Electrocoat is HLS Paint (Shanghai) Co., Ltd., the eighth generation of independent research and development of electrophoretic coating. This coating by epoxy acrylate modified, the film also has excellent corrosion resistance and weatherability, smooth appearance and full, suitable as a base topcoat system. In addition, the lead, cadmium, chromium, mercury and other heavy metals, two-component, water dispersible resin, at the same time, previous generations of the product characteristics, have good adaptability to the galvanized steel, almost can be applied to all metal coating, such as: cold hot rolled steel, galvanized steel, aluminum, zinc Aluminum Alloy plate, stainless steel plate.
The appearance of the coating is flat, delicate, smooth.
Good stability of bath can adaptable for a longer updating cycle.
The bath has strong anti-shrinkage and anti-pollution ability.
High penetration and good uniformity of internal and external.
Have excellent corrosion resistance and weathering resistance, especially suitable for the bottom surface of a painting system.
|
Pigment: carbon black, kaolin, antirust pigment
|
Solvent: alcohol ether |
|
Additives: surface active agent, prevent shrinkage cavity agent
|
|
|
Curing agent: totally enclosed multi-isocyanates
|
|
Product quality data :
| Project | Technical data | Test standard | ||
| Resin (HR-4000LB) | Color Paste | |||
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1000±500 | —— | HG/T 3334 |
| Appearance | —— | Milky white liquid | viscous liquid,no agglomeration | Visual |
| Storage stability | No stratified state, and there were no obvious difference compared to before storage |
In 5-35 ℃ temperature 1 year | ||
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Filling tank proportion and method :
⑴ Bath preparation
Ratio:
Resin 1400.00
Paste 233.00-175.00
DI water 1785.00
Total 3418.00-3360.00
⑵ Ripening conditions
Sample quantity: 3000～3500g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-35℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(165-185)℃×(20-30)min (Keeping temperature of parts coated)
Construction equipment :
|
Electrophoresis tank
|
Circulation devices (including filter, fill the paint device) | DI water equipment |
|
DC power supply and the power supply unit
|
Anode box (tube) and circulation device | Ultrafiltration device |
|
Cleaning devices
|
Heat exchanging equipment | Curing device |
Specification statement :
This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.