Product Details:
|
| Application Field: | Trench Pipe Fittings | Cooperation Case: | MEIDE GROUP |
|---|---|---|---|
| Performance: | Better Substrate Hiding | Main Ingredients: | Organic Acid ; Alcohol Ether |
| High Light: | electrophoretic coating,corrosion resistant coatings |
||
Trench pipe fittings high anticorrosive performance electrophoretic paint
Product Introduction :
HS-6060LB/HS-2568G Gray Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.
This product features shown below :
①,Good stability of bath can adaptable for a longer updating cycle.
②,Strong anti-corrosion properties, good salt spray resistance workpiece edge.
③,Coating fullness of good, better substrate hiding
④,Excellent leveling coating,good bonding force and compatibility with plastic powder
The main component Matrix resin :
|
Additives: surface active agent, prevent shrinkage cavity agent
|
Matrix resin: polyurethane modified epoxy resin |
|
Pigment: Titanium pigment, carbon black, kaolin, antirust pigment
|
Curing agent: totally enclosed multi-isocyanates |
Product film performance :
| Project | Indicator | Test standard | |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 72 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 48 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 1000 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Specification statement :
This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.
If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now
Customer production site :
Fax: 86-021-69122952