Elevator E Coat Paint , Electrocoat Corrosion Protection Coatings High Hardness

Good quality Cathodic Electrodeposition Paint for sales
Good quality Cathodic Electrodeposition Paint for sales
I'm Online Chat Now

Elevator E Coat Paint , Electrocoat Corrosion Protection Coatings High Hardness

China Elevator E Coat Paint , Electrocoat Corrosion Protection Coatings High Hardness supplier

Large Image :  Elevator E Coat Paint , Electrocoat Corrosion Protection Coatings High Hardness

Product Details:

Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HLS-1701ALB/HLS-1701A

Payment & Shipping Terms:

Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day
Contact Now
Detailed Product Description
Application Field: Elevator Parts Performance: High Hardness
Cooperation Case: LILONG Main Ingredients: Organic Acid ;antirust Pigment

The elevator makes high anticorrosion performance electrophoretic paint

 

Product Introduction :

 

HLS-1701ALB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.

 

It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal

 

such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.

 
This product features shown below : 

 

Have excellent corrosion resistance and weathering resistance, especially suitable for the bottom surface of a painting;

 

Strong anti-corrosion properties, good salt spray resistance workpiece edge.

 

Good stability of bath can adaptable for a longer updating cycle.

 

Coating fullness of good, better substrate hiding .


 
Main ingredients :
 

 

Pigmen:Titanium pigment, carbon black, kaolin, antirust pigment

 

 

Solvent::alcohol ether

 

 

Neutralizing agent :organic acid

 

 

Additives: surface active agent, prevent shrinkage cavity agent

 

 

Filling tank proportion and method :

 

⑴ Bath preparation

Ratio:

Resin 1200.00

Paste 200.00

DI water 2000.00


Total 3400.00

⑵ Ripening conditions

Sample quantity: 3000~5000g
Container: 5L (Diameter 16cm)

Tank temperature:28-30 ℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)


(3) Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 28-35℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions:(175-185)℃×(20-30)min (Keeping temperature of parts coated)


Construction equipment :

 

Cathodic electrophoretic coating construction in the electrophoresis tank, so need to have the following equipment: 

 

 

Electrophoresis tank 

 

Circulation devices (including filter, fill the paint device)  DI water equipment

 

DC power supply and the power supply unit 

 

Anode box (tube) and circulation device  Ultrafiltration device 

 

Cleaning devices 

 

Heat exchanging equipment  Curing device


Customers in the elevator industry :

 

Elevator E Coat Paint , Electrocoat Corrosion Protection Coatings High Hardness Elevator E Coat Paint , Electrocoat Corrosion Protection Coatings High Hardness

 

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)