Home
Products
About Us
Factory Tour
Quality Control
Contact Us
Request A Quote
Home ProductsGrey Electrophoretic Coating

Electric Vehicles Grey Electrophoretic Coating Film Smooth Performance

Good quality Cathodic Electrodeposition Paint for sales
Good quality Cathodic Electrodeposition Paint for sales
I'm Online Chat Now

Electric Vehicles Grey Electrophoretic Coating Film Smooth Performance

China Electric Vehicles Grey Electrophoretic Coating Film Smooth Performance supplier

Large Image :  Electric Vehicles Grey Electrophoretic Coating Film Smooth Performance

Product Details:

Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HS-6060LB/HS-2568G

Payment & Shipping Terms:

Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day
Contact Now
Detailed Product Description
Application Field: Electric Vehicles Performance: Film Smooth
Cooperation Case: SUNRA,LUYUAN Main Ingredients: Titanium Pigment;carbon Black, Kaolin

Grey electrophoretic paint for electric vehicles
 
Product Introduction:

 

 

HS-6060LB/HS-2568G Gray Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.

 

It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal,

 

such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.

 

 

 This product features shown below :

 

 
Good stability of bath can adaptable for a longer updating cycle. 

High penetration and good uniformity of internal and external. 

Have excellent corrosion resistance and weathering resistance, especially suitable for the bottom surface of a painting


Main ingredients:

 

Additives: surface active agent, prevent shrinkage cavity agent

 

Pigment: carbon black, kaolin, antirust pigment

 

Solvent: alcohol ether


 

Filling tank proportion and method :

 

⑴ Bath preparation

Ratio:

Resin                                1000.00-1250.00

Paste                                                250.00

DI water                            1900.00-2200.00


Total                                  3025.00-3575.00

⑵ Ripening conditions

Sample quantity: 3000~4000g
Container: 5L (Diameter 16cm)

Tank temperature:30 ±2 ℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)


 

Product film performance ​:

 

Project   Indicator Test standard
Appearance Normal / Abnormal Normal Ocular estimate
Hardness 2H GB/T 6739
Cup drawing mm, 6 GB/T 9753
Adhesion level 0 GB/T 9286
Flexibility mm 1 GB/T 1731
Impact Kg.cm 50 GB/T 1732
Gloss 60° 50-80 GB/T 9754
Water resistance h,(23±2)℃ ≥ 240 GB/T 1733
Acid resistance h(0.05N H2SO4) 72 GB/T 9274
Alkali resistance h(0.1N NaOH) 48 GB/T 9274
*Salt spray resistance film thickness ≥ 20μm  1000 GB/T 1771


* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.

 

Customers in the electric vehicles industry:

 

Electric Vehicles Grey Electrophoretic Coating Film Smooth Performance Electric Vehicles Grey Electrophoretic Coating Film Smooth Performance

 

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)