Product Details:
|
| Color: | Grey | Application Field: | High - Swimming Penetration Products |
|---|---|---|---|
| Performance: | High Throwing Power | Cooperation Case: | GEELY AUTO |
| High Light: | e coat paint,electrophoretic painting |
||
High throwing power (Four-box method)grey electrophoretic paint
Product Introduction :
HR-7001LB/HR-7010 Gray Cationic Epoxy Electrocoat for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS International Chemical Industry Group. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc
This product features shown below:
|
Strong anti-corrosion properties, good salt spray resistance workpiece edge
|
|
High throwing power, internal and external uniformity |
|
Coating fullness of good, better substrate hiding
|
|
suitable for auto body industry, such as cars, SUV and other models
|
The main component :
Pigment: Titanium pigment, carbon black, kaolin, antirust pigment
Additives: surface active agent, prevent shrinkage cavity agent, anti-yellowing agent.
Matrix resin: polyurethane modified epoxy resin
The main supplier :
|
Material name |
Supplier |
|
Polyisocyanates
|
Bayer |
|
Kaolin
|
Neuburg |
|
Carbon black
|
Cabot Corporation |
Bath on site management project :
Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:
| Classification | Project | Control Data | Testing frequency | |
| New bath | Anolyte | |||
| Electrophoresis tank | Ratio | 1:6 | -- | |
| Ripening time | 24-48 | -- | ||
| Solid ( 120 ℃ /1h ,% ) | 18±2 | -- | once a day | |
| PH | 5.8-6.2 | 2.0-3.5 | once a day | |
| Conductivity ( μs/cm ) | 1200±400 | 2000±1000 | once a day | |
| P/B | 0.20-0.35 | once a week | ||
| Throwing power (Four-box method), ≥ | ≥70% | once a year | ||
| Soluble(%) | Good appearance, coating survival rate≥95 | once a week | ||
| Solvent content (%) | 0.8-1.5 | once a week | ||
| Liquid level Fall head (cm ) | 10-15 | once a day | ||
| ED voltage( V ) | 0-300 | once a day | ||
| Break voltage ( V ) | ≥350 | once a week | ||
| Bath temperature ( ℃ ) | 32-36 | once a day | ||
| ED time( S ) | 60~180 | once a day | ||
| UF － 1 Tank | Solid content (%) | ≤2.0 | once a day | |
| UF － 2 Tank | Solid content (%) | ≤0.8 | once a day | |
| Baking furnace | Provisions furnace temperature( ℃ ) | 180-200 | once a day | |
| Curing conditions | Drying temperature | 165 ℃ (15-20)min (With content holding time) | once a day | |