IATF16949 Approved Electrophoretic Coating For Domestic Microwave Oven

Certification
China HLS Coatings (Shanghai)Co.Ltd certification
China HLS Coatings (Shanghai)Co.Ltd certification
I'm Online Chat Now

IATF16949 Approved Electrophoretic Coating For Domestic Microwave Oven

IATF16949 Approved Electrophoretic Coating For Domestic Microwave Oven
IATF16949 Approved Electrophoretic Coating For Domestic Microwave Oven

Large Image :  IATF16949 Approved Electrophoretic Coating For Domestic Microwave Oven

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HS-6600LB/HS-6060A
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day

IATF16949 Approved Electrophoretic Coating For Domestic Microwave Oven

Description
Main Ingredients: Organic Acid ;antirust Pigment Application Field: Microwave Oven
Performance: Color Uniformity Cooperation Case: Galanz
High Light:

cationic electrodeposition paint

,

ecoats

 

Electrophoretic coating for domestic microwave oven

 

Product Introduction :

 

HS-6060ALB/HS-6600 White Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.

It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.

 

This product features shown below: 

 

Excellent leveling coating,good bonding force and compatibility with plastic powder.

 

Strong anti-corrosion properties, good salt spray resistance workpiece edge.

 

Good stability of bath can adaptable for a longer updating cycl

 

 

Main ingredients:

 

 

 

Pigment: titanium dioxide, kaolin,antirust pigment

 

Neutralizing agent: organic acid

 

Additives: surface active agent, prevent shrinkage cavity agent,resistance to yellowing agent

 

 

 

Product quality data

 

Project Technical data Test standard
Resin
(HS-6060ALB)
White Paste (HS-6600)
pH 25℃ 6.0±1.0 —— GB/T 9724
Conductivity 25℃, μs/cm 1400±400 —— HG/T 3334
Appearance —— Milky white liquid White viscous liquid,no agglomeration Visual
Storage stability
No stratified state, and there were no obvious difference compared to before storage
In 5-35 ℃ temperature 1 year

 

Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution

 

 

Filling tank proportion and method

 

⑴ Bath preparation

Ratio:

Resin                       750.00-1000.00

Paste                                     250.00

DI water                 1900.00-2200.00


Total 3                    3025.00-3575.00

⑵ Ripening conditions

Sample quantity:  3000-4000g
Container: 5L (Diameter 16cm)

Tank temperature:28-30 ℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)


(3) Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 28-34 ℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions:(165-175)℃×(20-30)min (Keeping temperature of parts coated)

 

Customers in the microwave oven​ industry:

 