Water - Borne Electrophoretic Coating For Domestic Air Conditioning Industry

Certification
China HLS Coatings (Shanghai)Co.Ltd certification
China HLS Coatings (Shanghai)Co.Ltd certification
I'm Online Chat Now

Water - Borne Electrophoretic Coating For Domestic Air Conditioning Industry

Water - Borne Electrophoretic Coating For Domestic Air Conditioning Industry
Water - Borne Electrophoretic Coating For Domestic Air Conditioning Industry

Large Image :  Water - Borne Electrophoretic Coating For Domestic Air Conditioning Industry

Product Details:
Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HS-5400LB/HS-5400
Payment & Shipping Terms:
Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day

Water - Borne Electrophoretic Coating For Domestic Air Conditioning Industry

Description
Main Ingredients: Titanium Pigment;carbon Black, Kaolin Application Field: Air Conditioning
Performance: Film Smooth Cooperation Case: AUX,Chunlan
High Light:

ecoats

,

cationic epoxy electrocoat

Electrophoretic coating for domestic air conditioning industry

 

Product Introduction

 

HS-5400LB/HS-5400 White epoxy acrylic cathodic electrophoretic coating for auto is the 8th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS International Chemical Industry Group,and get the national invention patent and the Shanghai science and technology commission of high-tech transformation project.

It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin. The coating that does not contain tin element meet the latest environ-mental regulations of European Union, North America, Japan and other requirements in advance, which is the inevitable trend of future environ-mental coating and low cost; meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.

 

This product features shown below: 

 

Low curing temperature, coating yellow degeneration resistance is good, suitable for electrodeposition primer, and then to spray or paint coating process, such as: oil heater, radiator, heater, lamps and lanterns, machinery, home appliances and hardware products and other industries

 

 

Main ingredients:

 

Neutralizing agent organic acid
Pigment titanium dioxide, kaolin,antirust pigment
Additives surface active agent, prevent shrinkage cavity agent,resistance to yellowing agent

 

 

 

Filling tank proportion and method

 

⑴ Bath preparation

Ratio:

Resin                         800.00-1000.00

Paste                                       200.00

DI water                                 2000.00


Total 3                     3000.00-3200.00

⑵ Ripening conditions

Sample quantity:  3000-3200g
Container: 5L (Diameter 16cm)

Tank temperature:30 ±2℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)


(3) Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 30±2℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions:(150-170)℃×(20-30)min (Keeping temperature of parts coated)

 

Bath on site management project :

 

Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:

 

 

Classification Project Control Data Testing frequency
New bath Anolyte
Electrophoresis tank Ratio 1:(4-5) --  
Ripening time 24-48 --  
Solid ( 120 ℃ /1h ,% ) 12±2 -- once a day
PH 5.3-5.8 2.0-3.5 once a day
Conductivity ( μs/cm ) 900±400 1000±500 once a day
P/B 0.35-0.45 once a week
Solvent content (%) 1.2-2.0 once a week
Liquid level Fall head (cm ) 10-15 once a day
ED voltage( V ) 0-300 once a day
Break voltage ( V ) ≥350 once a week
Bath temperature ( ℃ ) 30±2 once a day
ED time( S ) 60~180 once a day
UF - 1 Tank Solid content (%) ≤2.0 once a day
UF - 2 Tank Solid content (%) ≤0.8 once a day
Baking furnace Provisions furnace temperature( ℃ ) 150-170 once a day
Curing conditions Drying temperature
(150-170)  ℃ x (15-20)min (With content holding time)
once a day

 

 

Customer production site :

 

Water - Borne Electrophoretic Coating For Domestic Air Conditioning Industry 0