High Penetration E Coat Car Coating , Electrocoat Paint Beautiful Appearance

Good quality Cathodic Electrodeposition Paint for sales
Good quality Cathodic Electrodeposition Paint for sales
I'm Online Chat Now

High Penetration E Coat Car Coating , Electrocoat Paint Beautiful Appearance

China High Penetration E Coat Car Coating , Electrocoat Paint Beautiful Appearance supplier

Large Image :  High Penetration E Coat Car Coating , Electrocoat Paint Beautiful Appearance

Product Details:

Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HR-4000BLB/HR-6000

Payment & Shipping Terms:

Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day
Contact Now
Detailed Product Description
Application Field: Lectric Vehicle Performance: Beautiful Appearance
Cooperation Case: SUNRA LUYUAN Main Ingredients: Totally Enclosed Multi-isocyanates

Solution for the electric vehicle electrophoresis paint​
 
Product Introduction:

 

 

HR-4000BLB/HR-6000 the bottom of one black cathode electrophoretic coating, is HLS Paint (Shanghai) Co., Ltd., the eighth generation of independent research and development of electrophoretic coating. This coating by epoxy acrylate modified, the film also has excellent corrosion resistance and weatherability, smooth appearance and full, suitable as a base topcoat system. In addition, the lead, cadmium, chromium, mercury and other heavy metals, two-component, water dispersible resin, at the same time, previous generations of the product characteristics, have good adaptability to the galvanized steel, almost can be applied to all metal coating,

such as: cold hot rolled steel, galvanized steel, aluminum, zinc Aluminum Alloy plate, stainless steel plate.

 

 

 

 This product features shown below:

 

 
Good stability of bath can adaptable for a longer updating cycle. 

High penetration and good uniformity of internal and external. 

Have excellent corrosion resistance and weathering resistance, especially suitable for the bottom surface of a painting

Main ingredients:

 

Solvent: alcohol ether
Additives: surface active agent, prevent shrinkage cavity agent
Pigment: carbon black, kaolin, antirust pigment
 

Filling tank proportion and method

 

⑴ Bath preparation

Ratio:

Resin                              10500.00-1400.00

Paste                                                175.00

​NHF-01                                                 2.00

DI water                                          1785.00


Total                                  3362.00-3012.00

⑵ Ripening conditions

Sample quantity: 3000~4500g
Container: 5L (Diameter 16cm)

Tank temperature:30 ±2 ℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)


 

Product film performance ​:

 

Project   Indicator Test standard
Appearance Normal / Abnormal Normal Ocular estimate
Hardness 2H GB/T 6739
Cup drawing mm, 7 GB/T 9753
Adhesion level 0 GB/T 9286
Flexibility mm 1 GB/T 1731
Impact Kg.cm 50 GB/T 1732
Gloss 60° 60-90 GB/T 9754
Water resistance h,(23±2)℃ ≥ 240 GB/T 1733
Acid resistance h(0.05N H2SO4) 72 GB/T 9274
Alkali resistance h(0.1N NaOH) 72 GB/T 9274
Weather resistanc h,(film thickness 20μm)≥ 600 GB/T 165
*Salt spray resistance film thickness ≥ 20μm  800 GB/T 1771


* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.

 

Customer production site:

 

High Penetration E Coat Car Coating , Electrocoat Paint Beautiful Appearance

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)