Electrolysis E Coating Car Body Painting With Better Substrate Hiding

Good quality Cathodic Electrodeposition Paint for sales
Good quality Cathodic Electrodeposition Paint for sales
I'm Online Chat Now

Electrolysis E Coating Car Body Painting With Better Substrate Hiding

China Electrolysis E Coating Car Body Painting With Better Substrate Hiding supplier

Large Image :  Electrolysis E Coating Car Body Painting With Better Substrate Hiding

Product Details:

Place of Origin: Shanghai China (Mainland)
Brand Name: HAOLISEN
Certification: IATF16949 , ISO9001
Model Number: HS-6060LB/HS-2668G

Payment & Shipping Terms:

Minimum Order Quantity: Negotiation
Price: Negotiation
Packaging Details: 50kg、60 kg、200kg、1000kg packaging barrels
Delivery Time: 30-60 Days
Supply Ability: 200 Tons Per Day
Contact Now
Detailed Product Description
Main Ingredients: Carbon Black, Kaolin Application Field: Car Covers
Performance: Film Smooth Cooperation Case: ANHUI Xin Hong Traffic,

Solution for the car covers electrophoresis paint.

 

Product Introduction

 

 HS-6060LB/HS-2668G Gray Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.

 

This product features shown below: 

 

 

Coating fullness of good, better substrate hiding .
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
The appearance of the coating is flat, delicate, smooth.
Good stability of bath can adaptable for a longer updating cycle. 
Excellent leveling coating,good bonding force and compatibility with plastic powder.

 

 

Filling tank proportion and method

 

⑴ Bath preparation

Ratio:

Resin                     1000.00-1250.00

Paste                                     250.00

DI water                               1500.00


Total                                     2750.00

⑵ Ripening conditions

Sample quantity 3000~4000g
Container 4L (Diameter 16cm)
Tank temperature 28-30 ℃
Time 24~48Hr
Mixed conditions impeller diameter 8cm (speed 200rpm)

 


(3) Coating conditions

Experimental panel phosphated cold-rolled steel plate
Tank temperature 28-35℃
Pole ratio A/C = 1/2 ~ 1/4
Distance of electrodes 15cm
ED time For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions (175-185)℃×(20-30)min (Keeping temperature of parts coated)

 


 

Product film performance

 

Project Indicator Test standard
Appearance Normal / abnormal Normal Ocular estimate
Hardness 2H GB/T 6739
Cup drawing mm ,≥ 6 GB/T 9753
Adhesion Level 0 GB/T 9286
Flexibility mm 1 GB/T 1731
Impact kg·cm 50 GB/T 1732
Gloss 60 50-80 GB/T 9754
Water resistance h,(23±2)℃,≥ 240 GB/T 1733
Acid resistance h,(50g/L H2SO4),≥ 72 GB/T 9274
Alkali resistance h,(50g/L NaOH),≥ 48 GB/T 9274
*Salt spray resistanc​e h,(film thickness ≥ 20μm) ,≥ 1000 GB/T 1771

* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.

 

 

Customer production site

 

Electrolysis E Coating Car Body Painting With Better Substrate Hiding

Contact Details
HLS Coatings (Shanghai)Co.Ltd

Contact Person: Penny

Tel: +8618049835525

Send your inquiry directly to us (0 / 3000)